EN 10088-3 X3CrNiCuMo17-11-3-2 vs EN 10088-1 X2CrNiMoN17-11-2

Close Alternative — 80.4% match based on chemical composition and mechanical property overlap.

EN 10088-3 X3CrNiCuMo17-11-3-2 (EN 10088-3:2014) and EN 10088-1 X2CrNiMoN17-11-2 (EN 10088-1:2023) are both steel grades. Both fall under the Stainless Steel category. EN 10088-3 X3CrNiCuMo17-11-3-2 is defined under European Standard (EN), originating from Europe, while EN 10088-1 X2CrNiMoN17-11-2 is defined under European Standard (EN), originating from Europe.

As per chemical composition, EN 10088-3 X3CrNiCuMo17-11-3-2 vs EN 10088-1 X2CrNiMoN17-11-2 is a 80.4% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 80.4%.

Frequently Compared With EN 10088-3 X3CrNiCuMo17-11-3-2:
GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
80.4%
MECHANICAL MATCH
No shared data
OVERALL
80.4%
Specifications
Property EN 10088-3 X3CrNiCuMo17-11-3-2 EN 10088-1 X2CrNiMoN17-11-2
Standard EN 10088-3:2014 EN 10088-1:2023
Category Stainless Steel Stainless Steel
C (%) <=0.04 <=0.030
Si (%) <=1.00 <=1.00
Mn (%) <=2.00 <=2.00
P (%) <=0.045 <=0.045
S (%) <=0.015 <=0.015
Cr (%) 16.5-17.5 16.5-18.5
Mo (%) 2.00-2.50 2.00-2.50
Ni (%) 10.0-11.0 10.0-12.5
N (%) <=0.10 0.12-0.22
Cu (%) 3.0-3.5 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-3 X3CrNiCuMo17-11-3-2 EN 10088-1 X2CrNiMoN17-11-2
Tensile Strength 450-650 MPa Not specified
Yield Strength >=175 MPa Not specified
Elongation >=45% Not specified
Hardness <=215 HB Not specified
Condition Solution annealed (+AT), conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal), hardness for guidance only Not specified
Typical Applications
EN 10088-3 X3CrNiCuMo17-11-3-2
General purposes, semi-finished products, bars, rods, wire, sections and bright products
EN 10088-1 X2CrNiMoN17-11-2
Not documented
Key Differences
Can EN 10088-3 X3CrNiCuMo17-11-3-2 Be Substituted With EN 10088-1 X2CrNiMoN17-11-2?
EN 10088-3 X3CrNiCuMo17-11-3-2 and EN 10088-1 X2CrNiMoN17-11-2 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
EN 10088-3 X3CrNiCuMo17-11-3-2
0 active listings and RFQs →
EN 10088-1 X2CrNiMoN17-11-2
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-3 X3CrNiCuMo17-11-3-2 and EN 10088-1 X2CrNiMoN17-11-2?
EN 10088-3 X3CrNiCuMo17-11-3-2 specifies Cu which is not specified for EN 10088-1 X2CrNiMoN17-11-2.
Can EN 10088-3 X3CrNiCuMo17-11-3-2 be substituted with EN 10088-1 X2CrNiMoN17-11-2?
EN 10088-3 X3CrNiCuMo17-11-3-2 and EN 10088-1 X2CrNiMoN17-11-2 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.