Close Alternative — 81.6% match
based on chemical composition and mechanical property overlap.
EN ISO 683-17 20CrMo4 (EN ISO 683-17:2014) and SAE J404 4135 (SAE J404:2009) are both steel grades.
Both fall under the Alloy Steel category.
EN ISO 683-17 20CrMo4 is typically used for used in gears, shafts, axles, high-tensile bolts, and structural components., while SAE J404 4135 is commonly used for gears, shafts, pressure vessels, high tensile bolts.
EN ISO 683-17 20CrMo4 is defined under European Standard (EN), originating from Europe, while SAE J404 4135 is defined under SAE International, originating from United States.
As per chemical composition, EN ISO 683-17 20CrMo4 vs SAE J404 4135 is a 81.6% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a close alternative overall at 81.6%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN ISO 683-17 20CrMo4
SAE J404 4135
Tensile Strength
700-850 MPa
Not specified
Yield Strength
500 MPa min
Not specified
Elongation
14% min
Not specified
Hardness
207-248 HB
Not specified
Typical Applications
EN ISO 683-17 20CrMo4
Used in gears, shafts, axles, high-tensile bolts, and structural components.
SAE J404 4135
Gears, shafts, pressure vessels, high tensile bolts
Can EN ISO 683-17 20CrMo4 Be Substituted With SAE J404 4135?
EN ISO 683-17 20CrMo4 and SAE J404 4135 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
What is the difference between EN ISO 683-17 20CrMo4 and SAE J404 4135?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN ISO 683-17 20CrMo4 be substituted with SAE J404 4135?
EN ISO 683-17 20CrMo4 and SAE J404 4135 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.