Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C
Si
Mn
B
Ti
P
S
Cu
0.22-0.28
0.20-0.45
1.30-1.60
0.0008-0.0035
0.04-0.10
<=0.030
<=0.030
<=0.30
Mechanical Properties
Tensile Strength
>=1380 MPa
Elongation
>=10%
Hardness
<=229 HB
Condition
Quenched and tempered, test sample Specimen (size not stated); hardness is for bars delivered annealed or high temperature tempered
More data from GB/T 3077:2015
From the standard
Recommended heat treatment5 settings
Test sample size
Specimen (size not stated)
Quenching temperature
860 deg C
Quenching coolant
oil
Tempering temperature
200 deg C
Tempering coolant
water, air
Allowable deviation: quenching +/-15 deg C, low temperature tempering +/-20 deg C, high temperature tempering +/-50 deg C.
Source: GB/T 3077:2015, Table 3
Mechanical properties, quenched and tempered6 values
Test sample size
Specimen (size not stated)
Tensile strength Rm, min
1380 MPa
Lower yield strength ReL, min
-
Elongation after fracture A, min
10 %
Reduction of area Z, min
40 %
Impact absorbed energy KU2, min
47 J
Minimum values after the recommended heat treatment; if sample is larger than the bar, treat the actual bar.
Source: GB/T 3077:2015, Table 3
Brinell hardness, annealed or high temperature tempered1 value
Brinell hardness HBW, max
229
For steel bars delivered annealed or high temperature tempered.
Source: GB/T 3077:2015, Table 3