GB/T 3077 25MnTiBRE vs BS 970 (Part 1) 175H23

Close Alternative — 74.8% match based on chemical composition and mechanical property overlap.

GB/T 3077 25MnTiBRE (GB/T 3077:2015) and BS 970 (Part 1) 175H23 (BS 970 (Part 1):1983) are both steel grades. Both fall under the Alloy Steel category. GB/T 3077 25MnTiBRE is typically used for hot-rolled or forged structural alloy steel bars, while BS 970 (Part 1) 175H23 is commonly used for case hardening steel supplied to specified hardenability limits (end quench test, table 10).. GB/T 3077 25MnTiBRE is defined under Guobiao Standards (GB/T), originating from China, while BS 970 (Part 1) 175H23 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, GB/T 3077 25MnTiBRE vs BS 970 (Part 1) 175H23 is a 74.8% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 74.8%.

Frequently Compared With GB/T 3077 25MnTiBRE:
IS 4367 07Cr4Mo6 IS 1570 (Part 4) 07Cr4Mo6 NF A35-565 100C6 UNI 11234 100Cr6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 7) 10Cr36Mo10H IS 4367 10Cr9Mo10 EN 10028-2 10CrMo9-10 IS 1570 (Part 4) 10Mo6
Match Breakdown
CHEMISTRY MATCH
74.8%
MECHANICAL MATCH
No shared data
OVERALL
74.8%
Specifications
Property GB/T 3077 25MnTiBRE BS 970 (Part 1) 175H23
Standard GB/T 3077:2015 BS 970 (Part 1):1983
Category Alloy Steel Alloy Steel
C (%) 0.22-0.28 0.20-0.25
Si (%) 0.20-0.45 Not specified
Mn (%) 1.30-1.60 1.30-1.60
B (%) 0.0008-0.0035 0.0005-0.005
Ti (%) 0.04-0.10 Not specified
P (%) <=0.030 <=0.060
S (%) <=0.030 0.03-0.06
Cu (%) <=0.30 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property GB/T 3077 25MnTiBRE BS 970 (Part 1) 175H23
Tensile Strength >=1380 MPa Not specified
Elongation >=10% Not specified
Hardness <=229 HB Not specified
Condition Quenched and tempered, test sample Specimen (size not stated); hardness is for bars delivered annealed or high temperature tempered Not specified
Typical Applications
GB/T 3077 25MnTiBRE
Hot-rolled or forged structural alloy steel bars
BS 970 (Part 1) 175H23
Case hardening steel supplied to specified hardenability limits (end quench test, Table 10).
Key Differences
Can GB/T 3077 25MnTiBRE Be Substituted With BS 970 (Part 1) 175H23?
GB/T 3077 25MnTiBRE and BS 970 (Part 1) 175H23 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
GB/T 3077 25MnTiBRE
0 active listings and RFQs →
BS 970 (Part 1) 175H23
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between GB/T 3077 25MnTiBRE and BS 970 (Part 1) 175H23?
GB/T 3077 25MnTiBRE specifies Si, Ti, Cu which are not specified for BS 970 (Part 1) 175H23.
Can GB/T 3077 25MnTiBRE be substituted with BS 970 (Part 1) 175H23?
GB/T 3077 25MnTiBRE and BS 970 (Part 1) 175H23 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.