GB/T 3077 20CrMnTi vs SAE J404 5120

Close Alternative — 76.4% match based on chemical composition and mechanical property overlap.

GB/T 3077 20CrMnTi (GB/T 3077:2015) and SAE J404 5120 (SAE J404:2009) are both steel grades. Both fall under the Alloy Steel category. GB/T 3077 20CrMnTi is typically used for gears, transmission shafts, pinions, carburized components, automotive parts, while SAE J404 5120 is commonly used for case hardened gears, pins, shafts, cams, automotive transmission parts. GB/T 3077 20CrMnTi is defined under Guobiao Standards (GB/T), originating from China, while SAE J404 5120 is defined under SAE International, originating from United States.

As per chemical composition, GB/T 3077 20CrMnTi vs SAE J404 5120 is a 76.4% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 76.4%.

Frequently Compared With GB/T 3077 20CrMnTi:
NF A35-565 100C6 GOST 4543 12HN3A UNI 11234 100Cr6 GB/T 3077 12Cr2Ni4A IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 103Cr4 IS 4367 07Cr4Mo6 IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 4) 103Cr6 IS 4367 10Cr9Mo10 IS 1570 (Part 7) 10Cr36Mo10H
Match Breakdown
CHEMISTRY MATCH
76.4%
MECHANICAL MATCH
No shared data
OVERALL
76.4%
Specifications
Property GB/T 3077 20CrMnTi SAE J404 5120
Standard GB/T 3077:2015 SAE J404:2009
Category Alloy Steel Alloy Steel
C (%) 0.17-0.23 0.17-0.22
Si (%) 0.17-0.37 0.15-0.35
Mn (%) 0.80-1.10 0.70-0.90
Cr (%) 1.00-1.30 0.70-0.90
Ti (%) 0.04-0.10 Not specified
P (%) <=0.030 <=0.030
S (%) <=0.030 <=0.040
Cu (%) <=0.30 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property GB/T 3077 20CrMnTi SAE J404 5120
Tensile Strength >=1080 MPa Not specified
Yield Strength >=850 MPa Not specified
Elongation >=10% Not specified
Hardness <=217 HB Not specified
Condition Quenched and tempered, test sample 15 mm; hardness is for bars delivered annealed or high temperature tempered Not specified
Typical Applications
GB/T 3077 20CrMnTi
gears, transmission shafts, pinions, carburized components, automotive parts
SAE J404 5120
Case hardened gears, pins, shafts, cams, automotive transmission parts
Key Differences
Can GB/T 3077 20CrMnTi Be Substituted With SAE J404 5120?
GB/T 3077 20CrMnTi and SAE J404 5120 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
Forms & Sizes Available on M-EX
GB/T 3077 20CrMnTi
Round Bar → (2 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 5500–6000 mm (216.54–236.22 in)
SAE J404 5120
Round Bar → (2 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 6200–6400 mm (244.09–251.97 in)
On M-EX Right Now
GB/T 3077 20CrMnTi
2 active listings and RFQs →
SAE J404 5120
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between GB/T 3077 20CrMnTi and SAE J404 5120?
GB/T 3077 20CrMnTi specifies Ti, Cu which are not specified for SAE J404 5120.
Can GB/T 3077 20CrMnTi be substituted with SAE J404 5120?
GB/T 3077 20CrMnTi and SAE J404 5120 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.