Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C
Si
Mn
Cr
Mo
P
S
Cu
0.32-0.40
0.17-0.37
0.40-0.70
0.80-1.10
0.15-0.25
<=0.030
<=0.030
<=0.30
Mechanical Properties
Tensile Strength
>=980 MPa
Yield Strength
>=835 MPa
Elongation
>=12%
Hardness
<=229 HB
Condition
Quenched and tempered, test sample 25 mm; hardness is for bars delivered annealed or high temperature tempered
More data from GB/T 3077:2015
From the standard
Recommended heat treatment5 settings
Test sample size
25 mm
Quenching temperature
850 deg C
Quenching coolant
oil
Tempering temperature
550 deg C
Tempering coolant
water, oil
Allowable deviation: quenching +/-15 deg C, low temperature tempering +/-20 deg C, high temperature tempering +/-50 deg C.
Source: GB/T 3077:2015, Table 3
Mechanical properties, quenched and tempered6 values
Test sample size
25 mm
Tensile strength Rm, min
980 MPa
Lower yield strength ReL, min
835 MPa
Elongation after fracture A, min
12 %
Reduction of area Z, min
45 %
Impact absorbed energy KU2, min
63 J
Minimum values after the recommended heat treatment; if sample is larger than the bar, treat the actual bar.
Source: GB/T 3077:2015, Table 3
Brinell hardness, annealed or high temperature tempered1 value
Brinell hardness HBW, max
229
For steel bars delivered annealed or high temperature tempered.