Close Alternative — 83.1% match based on chemical composition and mechanical property overlap.

GB/T 3077 35CrMo (GB/T 3077:2015) and SAE J404 4140 (SAE J404:2009) are both steel grades. Both fall under the Alloy Steel category. GB/T 3077 35CrMo is typically used for used for connecting rods, gears, shafts, bolts, spindles, and pressure vessel parts., while SAE J404 4140 is commonly used for gears, shafts, dies, bolts, crankshafts. GB/T 3077 35CrMo is defined under Guobiao Standards (GB/T), originating from China, while SAE J404 4140 is defined under SAE International, originating from United States.

As per chemical composition, GB/T 3077 35CrMo vs SAE J404 4140 is a 83.1% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 83.1%.

Frequently Compared With GB/T 3077 35CrMo:
UNI 11234 100Cr6 GB/T 3077 12Cr2Ni4A NF A35-565 100C6 GOST 4543 12HN3A IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 7) 10Cr36Mo10H IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 105Cr5 IS 4367 07Cr4Mo6 IS 1570 (Part 4) 103Cr4 IS 4367 10Cr9Mo10
Match Breakdown
CHEMISTRY MATCH
83.1%
MECHANICAL MATCH
No shared data
OVERALL
83.1%
Specifications
Property GB/T 3077 35CrMo SAE J404 4140
Standard GB/T 3077:2015 SAE J404:2009
Category Alloy Steel Alloy Steel
C (%) 0.32-0.40 0.38-0.43
Si (%) 0.17-0.37 0.15-0.35
Mn (%) 0.40-0.70 0.75-1.00
Cr (%) 0.80-1.10 0.80-1.10
Mo (%) 0.15-0.25 0.15-0.25
P (%) <=0.030 <=0.030
S (%) <=0.030 <=0.040
Cu (%) <=0.30 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property GB/T 3077 35CrMo SAE J404 4140
Tensile Strength >=980 MPa Not specified
Yield Strength >=835 MPa Not specified
Elongation >=12% Not specified
Hardness <=229 HB Not specified
Condition Quenched and tempered, test sample 25 mm; hardness is for bars delivered annealed or high temperature tempered Not specified
Typical Applications
GB/T 3077 35CrMo
Used for connecting rods, gears, shafts, bolts, spindles, and pressure vessel parts.
SAE J404 4140
Gears, shafts, dies, bolts, crankshafts
Key Differences
Can GB/T 3077 35CrMo Be Substituted With SAE J404 4140?
GB/T 3077 35CrMo and SAE J404 4140 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
Forms & Sizes Available on M-EX
GB/T 3077 35CrMo
Round Bar → (2 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 6400–6900 mm (251.97–271.65 in)
SAE J404 4140
Round Bar → (20 listings)
Diameter: 40–75 mm (1.57–2.95 in)
Length: 4800–6800 mm (188.98–267.72 in)
Hex Bar → (7 listings)
Across Flats: 40–60 mm (1.57–2.36 in)
Length: 2600–6100 mm (102.36–240.16 in)
Flat Bar → (6 listings)
Thickness: 35–40 mm (1.38–1.57 in)
Width: 180–180 mm (7.09–7.09 in)
Length: 2500–4400 mm (98.43–173.23 in)
On M-EX Right Now
GB/T 3077 35CrMo
2 active listings and RFQs →
SAE J404 4140
33 active listings and RFQs →
Frequently Asked Questions
What is the difference between GB/T 3077 35CrMo and SAE J404 4140?
GB/T 3077 35CrMo specifies Cu which is not specified for SAE J404 4140.
Can GB/T 3077 35CrMo be substituted with SAE J404 4140?
GB/T 3077 35CrMo and SAE J404 4140 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.