GB/T 700 Q275C (GB/T 700:2006) and GOST 19281 09G2S (GOST 19281-2014) are both steel grades. Both fall under the Structural Steel category. GB/T 700 Q275C is typically used for hot rolled structural sheets, strips, sections and bars for welding, riveting and bolting engineering, while GOST 19281 09G2S is commonly used for used for bridges, pressure vessels, pipelines, structural frames, and heavy equipment components.. GB/T 700 Q275C is defined under Guobiao Standards (GB/T) (China).

As per chemical composition, GB/T 700 Q275C vs GOST 19281 09G2S is a 65.8% match. As per mechanical properties, the match is 7.2%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With GB/T 700 Q275C:
CSA G40.21 260W AS/NZS 3679.1 300 CSA G40.21 300W AS/NZS 3679.1 350 CSA G40.21 400A CSA G40.21 400W ASTM A1008 SS Grade 80 ASTM A283C CSA G40.21 350W CSA G40.21 480W ASTM A1008 SS Grade 50 ASTM A572 Gr.65
Match Breakdown
CHEMISTRY MATCH
65.8%
MECHANICAL MATCH
7.2%
OVERALL
35%
Specifications
Property GB/T 700 Q275C GOST 19281 09G2S
Standard GB/T 700:2006 GOST 19281-2014
Category Structural Steel Structural Steel
C (%) <=0.20 0.07-0.12
Si (%) <=0.35 0.5-0.8
Mn (%) <=1.50 1.3-1.7
P (%) <=0.040 0.035 max
S (%) <=0.040 0.04 max
Ni (%) Not specified 0.3 max
Cr (%) Not specified 0.3 max
Cu (%) Not specified 0.3 max
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property GB/T 700 Q275C GOST 19281 09G2S
Tensile Strength 410-540 MPa 490-640 MPa
Yield Strength >=275 MPa 345 MPa min
Elongation >=22% 21% min
Condition Hot rolled, controlled rolled or normalized; yield up to 16 mm, elongation up to 40 mm (N/mm2 = MPa) Not specified
Hardness Not specified 140-190 HB
Typical Applications
GB/T 700 Q275C
Hot rolled structural sheets, strips, sections and bars for welding, riveting and bolting engineering
GOST 19281 09G2S
Used for bridges, pressure vessels, pipelines, structural frames, and heavy equipment components.
Key Differences
Can GB/T 700 Q275C Be Substituted With GOST 19281 09G2S?
GB/T 700 Q275C and GOST 19281 09G2S share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
GB/T 700 Q275C
No active listings currently.
GOST 19281 09G2S
Plate → (2 listings)
Thickness: 10–10 mm (0.39–0.39 in)
Width: 1500–1500 mm (59.06–59.06 in)
Length: 2900–3800 mm (114.17–149.61 in)
On M-EX Right Now
GB/T 700 Q275C
0 active listings and RFQs →
GOST 19281 09G2S
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between GB/T 700 Q275C and GOST 19281 09G2S?
GOST 19281 09G2S specifies Ni, Cr, Cu which are not specified for GB/T 700 Q275C.
Can GB/T 700 Q275C be substituted with GOST 19281 09G2S?
GB/T 700 Q275C and GOST 19281 09G2S share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.