GOST 1435 U10 vs EN ISO 4957 1.2316

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

GOST 1435 U10 (GOST 1435-1999) and EN ISO 4957 1.2316 (EN ISO 4957:2018) are both steel grades. Both fall under the Tool & Die Steels category. GOST 1435 U10 is typically used for used for chisels, punches, files, woodworking tools, and knives., while EN ISO 4957 1.2316 is commonly used for plastic injection moulds for corrosive materials, food packaging moulds. EN ISO 4957 1.2316 is defined under European Standard (EN) (Europe).

As per chemical composition, GOST 1435 U10 vs EN ISO 4957 1.2316 is a 54.5% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With GOST 1435 U10:
DIN EN ISO 4957 1.2344 DIN EN ISO 4957 1.2379 GB/T 1299 4Cr5MoSiV1 EN ISO 683-17 100Cr6 GB/T 1299 4Cr5MoSiV AISI 52100 GOST 5950 4H5MFS GOST 5950 3H2W8F GOST 5950 4H5MFS1 IS 1570 (Part 6) 103T3 IS 1570 (Part 6) 133T3 GB/T 1299 3Cr2W8V
Match Breakdown
CHEMISTRY MATCH
54.5%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property GOST 1435 U10 EN ISO 4957 1.2316
Standard GOST 1435-1999 EN ISO 4957:2018
Category Tool & Die Steels Tool & Die Steels
C (%) 0.95-1.04 ≤0.06
Mn (%) 0.17-0.33 ≤1.00
Si (%) 0.17-0.33 ≤0.50
S (%) 0.028 max Not specified
P (%) 0.03 max Not specified
Cr (%) Not specified 15.5–17.5
Mo (%) Not specified 0.80–1.30
Ni (%) Not specified 0.80–1.50
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property GOST 1435 U10 EN ISO 4957 1.2316
Tensile Strength 750-900 MPa Not specified
Yield Strength 450 MPa min Not specified
Elongation 10% min Not specified
Hardness 60-64 HRC Not specified
Hardness HRC Not specified 28–34 (pre-hardened)
Hardness HRC (hardened) Not specified 38–44
Corrosion Resistance Not specified Good in humid/corrosive environments
Typical Applications
GOST 1435 U10
Used for chisels, punches, files, woodworking tools, and knives.
EN ISO 4957 1.2316
Plastic injection moulds for corrosive materials, food packaging moulds
Key Differences
Can GOST 1435 U10 Be Substituted With EN ISO 4957 1.2316?
GOST 1435 U10 and EN ISO 4957 1.2316 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
GOST 1435 U10
Round Bar → (2 listings)
Diameter: 80–80 mm (3.15–3.15 in)
Length: 2800–3100 mm (110.24–122.05 in)
EN ISO 4957 1.2316
Round Bar → (2 listings)
Diameter: 80–80 mm (3.15–3.15 in)
Length: 2600–2700 mm (102.36–106.3 in)
On M-EX Right Now
GOST 1435 U10
2 active listings and RFQs →
EN ISO 4957 1.2316
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between GOST 1435 U10 and EN ISO 4957 1.2316?
GOST 1435 U10 specifies S, P which are not specified for EN ISO 4957 1.2316. EN ISO 4957 1.2316 specifies Cr, Mo, Ni which are not specified for GOST 1435 U10.
Can GOST 1435 U10 be substituted with EN ISO 4957 1.2316?
GOST 1435 U10 and EN ISO 4957 1.2316 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.