GOST 14959 60S2A vs UNI 11234 100Cr6

Minimal Match — 45.7% match based on chemical composition and mechanical property overlap.

GOST 14959 60S2A (GOST 14959-2016) and UNI 11234 100Cr6 (UNI 11234:2007) are both steel grades. Both fall under the Alloy Steel category. GOST 14959 60S2A is typically used for used for coil springs, suspension springs, washers, torsion bars, and railway springs., while UNI 11234 100Cr6 is commonly used for ball bearings,roller bearings,needle bearings,dies,punches,gauges,wear resistant components. UNI 11234 100Cr6 is defined under Ente Nazionale Italiano di Unificazione (UNI) (Italy).

As per chemical composition, GOST 14959 60S2A vs UNI 11234 100Cr6 is a 68.6% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 45.7%.

Frequently Compared With GOST 14959 60S2A:
GOST 4543 12HN3A NF A35-565 100C6 GB/T 3077 12Cr2Ni4A IS 1570 (Part 7) 10Cr36Mo10H IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 103Cr6 IS 4367 07Cr4Mo6 IS 1570 (Part 4) 10Cr20Mo6 IS 4367 10Cr9Mo10 EN 10028-2 10CrMo9-10
Match Breakdown
CHEMISTRY MATCH
68.6%
MECHANICAL MATCH
0%
OVERALL
45.7%
Specifications
Property GOST 14959 60S2A UNI 11234 100Cr6
Standard GOST 14959-2016 UNI 11234:2007
Category Alloy Steel Alloy Steel
C (%) 0.56-0.64 0.93-1.05
Si (%) 1.5-2.0 0.15-0.35
Mn (%) 0.6-0.9 0.25-0.45
Cr (%) 0.35 max 1.35-1.65
P (%) Not specified <=0.025
S (%) Not specified <=0.025
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property GOST 14959 60S2A UNI 11234 100Cr6
Tensile Strength 1270-1570 MPa 750-1000 MPa
Yield Strength 1080 MPa min 400-600 MPa
Elongation 6% min 10-14 %
Hardness 44-52 HRC 60-64 HRC
Typical Applications
GOST 14959 60S2A
Used for coil springs, suspension springs, washers, torsion bars, and railway springs.
UNI 11234 100Cr6
ball bearings,roller bearings,needle bearings,dies,punches,gauges,wear resistant components
Key Differences
Can GOST 14959 60S2A Be Substituted With UNI 11234 100Cr6?
GOST 14959 60S2A and UNI 11234 100Cr6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
GOST 14959 60S2A
Round Bar → (2 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 5400–5900 mm (212.6–232.28 in)
UNI 11234 100Cr6
Round Bar → (2 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 5700–6800 mm (224.41–267.72 in)
On M-EX Right Now
GOST 14959 60S2A
2 active listings and RFQs →
UNI 11234 100Cr6
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between GOST 14959 60S2A and UNI 11234 100Cr6?
UNI 11234 100Cr6 specifies P, S which are not specified for GOST 14959 60S2A.
Can GOST 14959 60S2A be substituted with UNI 11234 100Cr6?
GOST 14959 60S2A and UNI 11234 100Cr6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.