GOST 4543 15H2NM vs UNI 11234 100Cr6

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

GOST 4543 15H2NM (GOST 4543-2016) and UNI 11234 100Cr6 (UNI 11234:2007) are both steel grades. Both fall under the Alloy Steel category. GOST 4543 15H2NM is typically used for used for heavy-duty gears, shafts, couplings, bearings, and transmission parts., while UNI 11234 100Cr6 is commonly used for ball bearings,roller bearings,needle bearings,dies,punches,gauges,wear resistant components. UNI 11234 100Cr6 is defined under Ente Nazionale Italiano di Unificazione (UNI) (Italy).

As per chemical composition, GOST 4543 15H2NM vs UNI 11234 100Cr6 is a 60.3% match. As per mechanical properties, the match is 15.5%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With GOST 4543 15H2NM:
NF A35-565 100C6 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 105Cr5 GB/T 3077 12Cr2Ni4A IS 4367 07Cr4Mo6 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 7) 10Cr36Mo10H IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 103Cr4 IS 4367 10Cr9Mo10 IS 1570 (Part 4) 10Mo6 EN 10028-2 10CrMo9-10
Match Breakdown
CHEMISTRY MATCH
60.3%
MECHANICAL MATCH
15.5%
OVERALL
35%
Specifications
Property GOST 4543 15H2NM UNI 11234 100Cr6
Standard GOST 4543-2016 UNI 11234:2007
Category Alloy Steel Alloy Steel
C (%) 0.12-0.18 0.93-1.05
Cr (%) 1.25-1.65 1.35-1.65
Ni (%) 1.4-1.8 Not specified
Mo (%) 0.15-0.3 Not specified
Mn (%) 0.3-0.6 0.25-0.45
Si (%) Not specified 0.15-0.35
P (%) Not specified <=0.025
S (%) Not specified <=0.025
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property GOST 4543 15H2NM UNI 11234 100Cr6
Tensile Strength 900-1100 MPa 750-1000 MPa
Yield Strength 735 MPa min 400-600 MPa
Elongation 10% min 10-14 %
Hardness 58-62 HRC (case) 60-64 HRC
Typical Applications
GOST 4543 15H2NM
Used for heavy-duty gears, shafts, couplings, bearings, and transmission parts.
UNI 11234 100Cr6
ball bearings,roller bearings,needle bearings,dies,punches,gauges,wear resistant components
Key Differences
Can GOST 4543 15H2NM Be Substituted With UNI 11234 100Cr6?
GOST 4543 15H2NM and UNI 11234 100Cr6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
GOST 4543 15H2NM
Round Bar → (2 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 6000–6500 mm (236.22–255.91 in)
UNI 11234 100Cr6
Round Bar → (2 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 5700–6800 mm (224.41–267.72 in)
On M-EX Right Now
GOST 4543 15H2NM
2 active listings and RFQs →
UNI 11234 100Cr6
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between GOST 4543 15H2NM and UNI 11234 100Cr6?
GOST 4543 15H2NM specifies Ni, Mo which are not specified for UNI 11234 100Cr6. UNI 11234 100Cr6 specifies Si, P, S which are not specified for GOST 4543 15H2NM.
Can GOST 4543 15H2NM be substituted with UNI 11234 100Cr6?
GOST 4543 15H2NM and UNI 11234 100Cr6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.