Minimal Match — 40.4% match based on chemical composition and mechanical property overlap.

GOST 5950 9HVG (GOST 5950-2000) and GB/T 1299 3Cr2W8V (GB/T 1299-2014) are both steel grades. Both fall under the Tool & Die Steels category. GOST 5950 9HVG is typically used for used for broaches, taps, dies, punches, and precision cutting tools., while GB/T 1299 3Cr2W8V is commonly used for used for hot forging dies, extrusion dies, die-casting molds, hot punches, and hot shear blades.. GB/T 1299 3Cr2W8V is defined under Guobiao Standards (GB/T) (China).

As per chemical composition, GOST 5950 9HVG vs GB/T 1299 3Cr2W8V is a 60.5% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 40.4%.

Frequently Compared With GOST 5950 9HVG:
GOST 5950 4H5MFS1 EN ISO 4957 1.2316 GB/T 1299 4Cr5MoSiV1 GOST 5950 4H5MFS DIN EN ISO 4957 1.2379 AISI 52100 GB/T 1299 4Cr5MoSiV DIN EN ISO 4957 1.2344 GOST 5950 3H2W8F EN ISO 683-17 100Cr6
Other Tool & Die Steels Grades to Compare With GOST 5950 9HVG:
IS 3748 103T3 IS 1570 (Part 6) 103T3
Match Breakdown
CHEMISTRY MATCH
60.5%
MECHANICAL MATCH
0%
OVERALL
40.4%
Specifications
Property GOST 5950 9HVG GB/T 1299 3Cr2W8V
Standard GOST 5950-2000 GB/T 1299-2014
Category Tool & Die Steels Tool & Die Steels
C (%) 0.85-0.95 0.30-0.40
Cr (%) 0.9-1.2 2.20-2.70
W (%) 0.9-1.2 7.50-9.00
Mn (%) 0.8-1.1 0.20-0.50
Si (%) 0.15-0.35 0.20-0.40
V (%) Not specified 0.20-0.50
P (%) Not specified 0.030 max
S (%) Not specified 0.030 max
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property GOST 5950 9HVG GB/T 1299 3Cr2W8V
Tensile Strength 950-1150 MPa 1180-1380 MPa
Yield Strength 750 MPa min 980-1180 MPa
Elongation 7% min 10-14%
Hardness 61-65 HRC 48-54 HRC
Typical Applications
GOST 5950 9HVG
Used for broaches, taps, dies, punches, and precision cutting tools.
GB/T 1299 3Cr2W8V
Used for hot forging dies, extrusion dies, die-casting molds, hot punches, and hot shear blades.
Key Differences
Can GOST 5950 9HVG Be Substituted With GB/T 1299 3Cr2W8V?
GOST 5950 9HVG and GB/T 1299 3Cr2W8V share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
GOST 5950 9HVG
Round Bar → (2 listings)
Diameter: 80–80 mm (3.15–3.15 in)
Length: 2500–3100 mm (98.43–122.05 in)
GB/T 1299 3Cr2W8V
Round Bar → (2 listings)
Diameter: 80–80 mm (3.15–3.15 in)
Length: 2800–2900 mm (110.24–114.17 in)
On M-EX Right Now
GOST 5950 9HVG
2 active listings and RFQs →
GB/T 1299 3Cr2W8V
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between GOST 5950 9HVG and GB/T 1299 3Cr2W8V?
GB/T 1299 3Cr2W8V specifies V, P, S which are not specified for GOST 5950 9HVG.
Can GOST 5950 9HVG be substituted with GB/T 1299 3Cr2W8V?
GOST 5950 9HVG and GB/T 1299 3Cr2W8V share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.