Strong Match — 87.7% match
based on chemical composition and mechanical property overlap.
IS 11169 (Part 1) 15Ni16Cr5 (IS 11169 (Part 1):1984) and IS 4367 15Ni16Cr5 (IS 4367:1991) are both steel grades.
Both fall under the Alloy Steel category.
IS 11169 (Part 1) 15Ni16Cr5 is typically used for cold heading and cold extrusion; the standard covers wires, wire rods and bars of 2 to 100 mm diameter (clause 1.1), while IS 4367 15Ni16Cr5 is commonly used for aircraft gears, heavy duty gears, transmission shafts, camshafts, automotive components.
IS 11169 (Part 1) 15Ni16Cr5 is defined under Bureau of Indian Standards (IS), originating from India, while IS 4367 15Ni16Cr5 is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, IS 11169 (Part 1) 15Ni16Cr5 vs IS 4367 15Ni16Cr5 is a 98.3% match.
As per mechanical properties, the match is 66.7%.
Combined, this makes them a strong match overall at 87.7%.
Frequently Compared With IS 11169 (Part 1) 15Ni16Cr5:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Refined, quenched and stress relieved (core properties), ruling section up to 30 mm
Typical Applications
IS 11169 (Part 1) 15Ni16Cr5
Cold heading and cold extrusion; the standard covers wires, wire rods and bars of 2 to 100 mm diameter (clause 1.1)
IS 4367 15Ni16Cr5
aircraft gears, heavy duty gears, transmission shafts, camshafts, automotive components
Key Differences
IS 4367 15Ni16Cr5 specifies S, P which are not specified for IS 11169 (Part 1) 15Ni16Cr5.
Can IS 11169 (Part 1) 15Ni16Cr5 Be Substituted With IS 4367 15Ni16Cr5?
IS 11169 (Part 1) 15Ni16Cr5 and IS 4367 15Ni16Cr5 overlap closely enough on chemistry and mechanical properties that IS 4367 15Ni16Cr5 is often considered as a substitute for IS 11169 (Part 1) 15Ni16Cr5 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between IS 11169 (Part 1) 15Ni16Cr5 and IS 4367 15Ni16Cr5?
IS 4367 15Ni16Cr5 specifies S, P which are not specified for IS 11169 (Part 1) 15Ni16Cr5.
Can IS 11169 (Part 1) 15Ni16Cr5 be substituted with IS 4367 15Ni16Cr5?
IS 11169 (Part 1) 15Ni16Cr5 and IS 4367 15Ni16Cr5 overlap closely enough on chemistry and mechanical properties that IS 4367 15Ni16Cr5 is often considered as a substitute for IS 11169 (Part 1) 15Ni16Cr5 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.