IS 11169 (Part 1) 40Cr4Mo3 vs IS 4367 07Cr4Mo6

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 1) 40Cr4Mo3 (IS 11169 (Part 1):1984) and IS 4367 07Cr4Mo6 (IS 4367:1991) are both steel grades. Both fall under the Alloy Steel category. IS 11169 (Part 1) 40Cr4Mo3 is defined under Bureau of Indian Standards (IS), originating from India, while IS 4367 07Cr4Mo6 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 11169 (Part 1) 40Cr4Mo3 vs IS 4367 07Cr4Mo6 is a 62.6% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With IS 11169 (Part 1) 40Cr4Mo3:
IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 7) 10Cr36Mo10H IS 4367 10Cr9Mo10 IS 1570 (Part 4) 10Mo6 IS 1570 (Part 7) 10Mo6H UNI 11234 100Cr6 IS 1570 (Part 4) 10Cr20Mo6 NF A35-565 100C6 IS 11169 (Part 1) 10Ni5Cr4
Match Breakdown
CHEMISTRY MATCH
62.6%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property IS 11169 (Part 1) 40Cr4Mo3 IS 4367 07Cr4Mo6
Standard IS 11169 (Part 1):1984 IS 4367:1991
Category Alloy Steel Alloy Steel
C (%) 0.35-0.45 <=0.12
Mn (%) 0.50-0.80 0.40-0.70
Si (%) 0.10-0.35 0.15-0.60
Cr (%) 0.90-1.20 0.70-1.10
Mo (%) 0.20-0.35 0.45-0.65
Ni (%) Not specified <=0.30
S (%) Not specified <=0.035
P (%) Not specified <=0.035
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 1) 40Cr4Mo3 IS 4367 07Cr4Mo6
Tensile Strength (hardened and tempered) 1100-1300 MPa (16 mm) / 1000-1200 MPa (40 mm) / 900-1100 MPa (100 mm) Not specified
0.2% Proof Stress >=900 MPa (16 mm) / >=750 MPa (40 mm) / >=700 MPa (100 mm) Not specified
Elongation >=10% (16 mm) / >=11% (40 mm) / >=12% (100 mm) >=19%
Hardness, annealed <=200 HB Not specified
Tensile Strength Not specified 380-550 MPa
Yield Strength Not specified 225 MPa min
Izod Impact Not specified 60 J min
Hardness (soft annealed) Not specified <=170 HB
Condition Not specified Normalised and tempered, ruling section up to 40 mm
Typical Applications
IS 11169 (Part 1) 40Cr4Mo3
Cold heading and cold extrusion; the standard covers wires, wire rods and bars of 2 to 100 mm diameter (clause 1.1)
IS 4367 07Cr4Mo6
Not documented
Key Differences
Can IS 11169 (Part 1) 40Cr4Mo3 Be Substituted With IS 4367 07Cr4Mo6?
IS 11169 (Part 1) 40Cr4Mo3 and IS 4367 07Cr4Mo6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
IS 11169 (Part 1) 40Cr4Mo3
0 active listings and RFQs →
IS 4367 07Cr4Mo6
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 1) 40Cr4Mo3 and IS 4367 07Cr4Mo6?
IS 4367 07Cr4Mo6 specifies Ni, S, P which are not specified for IS 11169 (Part 1) 40Cr4Mo3.
Can IS 11169 (Part 1) 40Cr4Mo3 be substituted with IS 4367 07Cr4Mo6?
IS 11169 (Part 1) 40Cr4Mo3 and IS 4367 07Cr4Mo6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.