IS 11169 (Part 1) 16Ni4Cr3 vs BS 970 (Part 1) 637H17

Strong Match — 86.5% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 1) 16Ni4Cr3 (IS 11169 (Part 1):2022) and BS 970 (Part 1) 637H17 (BS 970 (Part 1):1983) are both steel grades. Both fall under the Alloy Steel category. IS 11169 (Part 1) 16Ni4Cr3 is typically used for cold heading and cold extrusion of parts that are case hardened; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, annex b), while BS 970 (Part 1) 637H17 is commonly used for case hardening steel supplied to specified hardenability limits (end quench test, table 10).. IS 11169 (Part 1) 16Ni4Cr3 is defined under Bureau of Indian Standards (IS), originating from India, while BS 970 (Part 1) 637H17 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, IS 11169 (Part 1) 16Ni4Cr3 vs BS 970 (Part 1) 637H17 is a 86.5% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 86.5%.

Frequently Compared With IS 11169 (Part 1) 16Ni4Cr3:
NF A35-565 100C6 IS 1570 (Part 4) 07Cr4Mo6 UNI 11234 100Cr6 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 10Cr20Mo6 IS 4367 10Cr9Mo10 IS 4367 07Cr4Mo6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 7) 10Cr36Mo10H IS 1570 (Part 4) 10Mo6 IS 1570 (Part 7) 10Mo6H
Match Breakdown
CHEMISTRY MATCH
86.5%
MECHANICAL MATCH
No shared data
OVERALL
86.5%
Specifications
Property IS 11169 (Part 1) 16Ni4Cr3 BS 970 (Part 1) 637H17
Standard IS 11169 (Part 1):2022 BS 970 (Part 1):1983
Category Alloy Steel Alloy Steel
C (%) 0.12-0.20 0.14-0.20
Cr (%) 0.60-1.00 0.60-1.00
Cu (%) <=0.15 Not specified
Mn (%) 0.60-1.00 0.60-0.90
Mo (%) <=0.05 Not specified
Ni (%) 0.80-1.20 0.85-1.25
P (%) <=0.035 <=0.035
S (%) <=0.035 <=0.040
Si (%) 0.10-0.35 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 1) 16Ni4Cr3 BS 970 (Part 1) 637H17
Hardness, annealed (+AC) <=180 HBW Not specified
Typical Applications
IS 11169 (Part 1) 16Ni4Cr3
Cold heading and cold extrusion of parts that are case hardened; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, Annex B)
BS 970 (Part 1) 637H17
Case hardening steel supplied to specified hardenability limits (end quench test, Table 10).
Key Differences
Can IS 11169 (Part 1) 16Ni4Cr3 Be Substituted With BS 970 (Part 1) 637H17?
IS 11169 (Part 1) 16Ni4Cr3 and BS 970 (Part 1) 637H17 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 1) 637H17 is often considered as a substitute for IS 11169 (Part 1) 16Ni4Cr3 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 11169 (Part 1) 16Ni4Cr3
0 active listings and RFQs →
BS 970 (Part 1) 637H17
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 1) 16Ni4Cr3 and BS 970 (Part 1) 637H17?
IS 11169 (Part 1) 16Ni4Cr3 specifies Cu, Mo, Si which are not specified for BS 970 (Part 1) 637H17.
Can IS 11169 (Part 1) 16Ni4Cr3 be substituted with BS 970 (Part 1) 637H17?
IS 11169 (Part 1) 16Ni4Cr3 and BS 970 (Part 1) 637H17 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 1) 637H17 is often considered as a substitute for IS 11169 (Part 1) 16Ni4Cr3 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.