IS 11169 (Part 1) 17C8GC (case hardening) vs EN 10084 C16E

Strong Match — 89.8% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 1) 17C8GC (case hardening) (IS 11169 (Part 1):2022) and EN 10084 C16E (EN 10084:2008) are both steel grades. Both fall under the Carbon Steel category. IS 11169 (Part 1) 17C8GC (case hardening) is typically used for cold heading and cold extrusion of parts that are case hardened; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, annex b), while EN 10084 C16E is commonly used for case hardened machine parts: carburized or carbonitrided, then hardened (clause 3.1). IS 11169 (Part 1) 17C8GC (case hardening) is defined under Bureau of Indian Standards (IS), originating from India, while EN 10084 C16E is defined under European Standard (EN), originating from Europe.

As per chemical composition, IS 11169 (Part 1) 17C8GC (case hardening) vs EN 10084 C16E is a 89.8% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 89.8%.

Frequently Compared With IS 11169 (Part 1) 17C8GC (case hardening):
BS 970 (Part 1) 040A10 BS 970 (Part 3) 070M55 BS 970 (Part 1) 045M10 BS 970 (Part 3) 045M10 BS 970 (Part 1) 055M15 BS 970 (Part 1) 060A32 BS 970 (Part 1) 040A04 BS 970 (Part 1) 040A12 BS 970 (Part 1) 045A10 BS 970 (Part 1) 045A10 BS 970 (Part 3) 045A10 BS 970 (Part 1) 045M10
Match Breakdown
CHEMISTRY MATCH
89.8%
MECHANICAL MATCH
No shared data
OVERALL
89.8%
Specifications
Property IS 11169 (Part 1) 17C8GC (case hardening) EN 10084 C16E
Standard IS 11169 (Part 1):2022 EN 10084:2008
Category Carbon Steel Carbon Steel
C (%) 0.15-0.19 0.12-0.18
Cu (%) <=0.25 Not specified
Mn (%) 0.60-0.90 0.60-0.90
P (%) <=0.025 <=0.035
S (%) <=0.025 <=0.035
Si (%) <=0.30 <=0.40
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 1) 17C8GC (case hardening) EN 10084 C16E
Tensile Strength, as rolled (+AR) <=530 MPa (over 5 to 100 mm) Not specified
Condition Not specified Soft annealed
Hardness Not specified Soft annealed: 156 HB max
Typical Applications
IS 11169 (Part 1) 17C8GC (case hardening)
Cold heading and cold extrusion of parts that are case hardened; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, Annex B)
EN 10084 C16E
Case hardened machine parts: carburized or carbonitrided, then hardened (clause 3.1)
Key Differences
Can IS 11169 (Part 1) 17C8GC (case hardening) Be Substituted With EN 10084 C16E?
IS 11169 (Part 1) 17C8GC (case hardening) and EN 10084 C16E overlap closely enough on chemistry and mechanical properties that EN 10084 C16E is often considered as a substitute for IS 11169 (Part 1) 17C8GC (case hardening) in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 11169 (Part 1) 17C8GC (case hardening)
0 active listings and RFQs →
EN 10084 C16E
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 1) 17C8GC (case hardening) and EN 10084 C16E?
IS 11169 (Part 1) 17C8GC (case hardening) specifies Cu which is not specified for EN 10084 C16E.
Can IS 11169 (Part 1) 17C8GC (case hardening) be substituted with EN 10084 C16E?
IS 11169 (Part 1) 17C8GC (case hardening) and EN 10084 C16E overlap closely enough on chemistry and mechanical properties that EN 10084 C16E is often considered as a substitute for IS 11169 (Part 1) 17C8GC (case hardening) in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.