IS 11169 (Part 1) 18C10BT vs BS 970 (Part 1) 170H20

Close Alternative — 82.9% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 1) 18C10BT (IS 11169 (Part 1):2022) and BS 970 (Part 1) 170H20 (BS 970 (Part 1):1983) are both steel grades. Both fall under the Alloy Steel category. IS 11169 (Part 1) 18C10BT is typically used for cold heading and cold extrusion of parts that are case hardened; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, annex b), while BS 970 (Part 1) 170H20 is commonly used for through hardening steel for mechanical and allied engineering purposes (table 6 gives composition only; see the hardenability tables).. IS 11169 (Part 1) 18C10BT is defined under Bureau of Indian Standards (IS), originating from India, while BS 970 (Part 1) 170H20 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, IS 11169 (Part 1) 18C10BT vs BS 970 (Part 1) 170H20 is a 82.9% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 82.9%.

Frequently Compared With IS 11169 (Part 1) 18C10BT:
IS 1570 (Part 4) 10Cr20Mo6 IS 4367 07Cr4Mo6 NF A35-565 100C6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 7) 10Cr36Mo10H IS 1570 (Part 4) 10Mo6 IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 105Cr5 IS 4367 10Cr9Mo10 UNI 11234 100Cr6 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 7) 10Mo6H
Match Breakdown
CHEMISTRY MATCH
82.9%
MECHANICAL MATCH
No shared data
OVERALL
82.9%
Specifications
Property IS 11169 (Part 1) 18C10BT BS 970 (Part 1) 170H20
Standard IS 11169 (Part 1):2022 BS 970 (Part 1):1983
Category Alloy Steel Alloy Steel
B (%) 0.0008-0.005 0.0005-0.005
C (%) 0.16-0.20 0.17-0.23
Cu (%) <=0.25 Not specified
Mn (%) 0.90-1.20 0.80-1.10
P (%) <=0.025 <=0.035
S (%) <=0.025 <=0.040
Si (%) <=0.30 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 1) 18C10BT BS 970 (Part 1) 170H20
Tensile Strength, as rolled (+AR) <=580 MPa (over 5 to 40 mm) Not specified
Typical Applications
IS 11169 (Part 1) 18C10BT
Cold heading and cold extrusion of parts that are case hardened; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, Annex B)
BS 970 (Part 1) 170H20
Through hardening steel for mechanical and allied engineering purposes (Table 6 gives composition only; see the hardenability tables).
Key Differences
Can IS 11169 (Part 1) 18C10BT Be Substituted With BS 970 (Part 1) 170H20?
IS 11169 (Part 1) 18C10BT and BS 970 (Part 1) 170H20 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
IS 11169 (Part 1) 18C10BT
0 active listings and RFQs →
BS 970 (Part 1) 170H20
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 1) 18C10BT and BS 970 (Part 1) 170H20?
IS 11169 (Part 1) 18C10BT specifies Cu, Si which are not specified for BS 970 (Part 1) 170H20.
Can IS 11169 (Part 1) 18C10BT be substituted with BS 970 (Part 1) 170H20?
IS 11169 (Part 1) 18C10BT and BS 970 (Part 1) 170H20 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.