IS 11169 (Part 1):2022 20C8GC Steel: Specifications & Listings
IS 11169 (Part 1):2022 20C8GC: Cold heading quality non-alloy steel 20C8GC to IS 11169 (Part 1):2022, for parts that are not heat treated after cold heading or cold extrusion, supplied as wire rod, bars or wire of 2 to 100 mm. Maximum tensile strength as hot rolled is 560 MPa.
Cold heading and cold extrusion of parts not heat treated after cold forming; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, Annex A)
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
Al
C
Cr
Cu
Mn
Mo
Ni
P
S
Si
<=0.015
0.18-0.22
<=0.30
<=0.30
0.70-0.90
<=0.10
<=0.30
<=0.025
<=0.025
0.15-0.25
Mechanical Properties
Reduction of Area, as rolled (+AR)
>=55% (for information)
Tensile Strength, as rolled (+AR)
<=560 MPa (over 5 to 100 mm)
More data from IS 11169 (Part 1):2022
From the standard
Other composition limitsfrom the table notes and clauses
Values
Maximum unless a range is given (ladle analysis)
Cr + Ni + Mo, maximum
0.50 percent
Aluminium
May be replaced by another element or elements with a similar effect
Manganese
A lower manganese content may be specified, with a range of 0.20 percent
Deoxidation
Killed steel; aluminium killed, silicon killed or both (clause 6.2)
Elements not listed are not added intentionally without the purchaser's agreement, except those used to finish the heat.
Source: IS 11169 (Part 1):2022, Table A.2 and its notes, clause 6.2
Tensile strength and reduction of area by delivery conditionby delivery condition and size
Delivery condition
Diameter (mm)
Tensile strength, max (MPa)
Reduction of area, min (%)
+AR or +AR+PE
over 5 to 10
560
55
+AR or +AR+PE
over 10 to 40
560
55
+AR or +AR+PE
over 40 to 100
560
55
+AC or +AC+PE
over 5 to 10
480
65
+AC or +AC+PE
over 10 to 40
480
65
+AC or +AC+PE
over 40 to 100
480
65
+AR+C
over 5 to 10
650
53
+AR+C
over 10 to 40
640
53
+AR+C+AC
2 (incl.) to 5
470
67
+AR+C+AC
over 5 to 10
460
67
+AR+C+AC
over 10 to 40
460
67
+AR+C+AC+LC
2 (incl.) to 5
510
63
+AR+C+AC+LC
over 5 to 10
500
63
+AR+C+AC+LC
over 10 to 40
500
63
+AC+C
over 5 to 10
570
60
+AC+C
over 10 to 40
560
60
Codes: +AR as hot rolled, +PE peeled, +C cold drawn, +AC annealed to spheroidized carbides, +LC skin passed. Reduction of area values are for information only. For non-circular sections the properties are agreed between manufacturer and purchaser.
Source: IS 11169 (Part 1):2022, Table A.3