IS 11169 (Part 1) 20C8GC vs IS 11169 (Part 1) 20Ni2Cr2Mo3

Related Material — 65% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 1) 20C8GC (IS 11169 (Part 1):2022) and IS 11169 (Part 1) 20Ni2Cr2Mo3 (IS 11169 (Part 1):2022) are both steel grades. IS 11169 (Part 1) 20C8GC is classified under Carbon Steel, while IS 11169 (Part 1) 20Ni2Cr2Mo3 is classified under Alloy Steel — a different category, which is worth noting alongside the chemistry match below. IS 11169 (Part 1) 20C8GC is typically used for cold heading and cold extrusion of parts not heat treated after cold forming; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, annex a), while IS 11169 (Part 1) 20Ni2Cr2Mo3 is commonly used for cold heading and cold extrusion of parts that are case hardened; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, annex b). IS 11169 (Part 1) 20C8GC is defined under Bureau of Indian Standards (IS), originating from India, while IS 11169 (Part 1) 20Ni2Cr2Mo3 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 11169 (Part 1) 20C8GC vs IS 11169 (Part 1) 20Ni2Cr2Mo3 is a 65.8% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 65%.

Frequently Compared With IS 11169 (Part 1) 20C8GC:
BS 970 (Part 1) 040A10 BS 970 (Part 3) 070M55 BS 970 (Part 1) 045M10 BS 970 (Part 1) 040A04 BS 970 (Part 1) 040A12 BS 970 (Part 1) 045A10 BS 970 (Part 1) 045A10 BS 970 (Part 1) 045M10 BS 970 (Part 1) 060A32 BS 970 (Part 3) 045A10 BS 970 (Part 3) 045M10 BS 970 (Part 1) 055M15
Match Breakdown
CHEMISTRY MATCH
65.8%
MECHANICAL MATCH
No shared data
OVERALL
65%
Specifications
Property IS 11169 (Part 1) 20C8GC IS 11169 (Part 1) 20Ni2Cr2Mo3
Standard IS 11169 (Part 1):2022 IS 11169 (Part 1):2022
Category Carbon Steel Alloy Steel
Al (%) <=0.015 Not specified
C (%) 0.18-0.22 0.18-0.23
Cr (%) <=0.30 0.40-0.60
Cu (%) <=0.30 <=0.35
Mn (%) 0.70-0.90 0.70-0.90
Mo (%) <=0.10 0.20-0.30
Ni (%) <=0.30 0.40-0.70
P (%) <=0.025 <=0.030
S (%) <=0.025 <=0.040
Si (%) 0.15-0.25 0.15-0.35
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 1) 20C8GC IS 11169 (Part 1) 20Ni2Cr2Mo3
Reduction of Area, as rolled (+AR) >=55% (for information) Not specified
Tensile Strength, as rolled (+AR) <=560 MPa (over 5 to 100 mm) Not specified
Typical Applications
IS 11169 (Part 1) 20C8GC
Cold heading and cold extrusion of parts not heat treated after cold forming; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, Annex A)
IS 11169 (Part 1) 20Ni2Cr2Mo3
Cold heading and cold extrusion of parts that are case hardened; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, Annex B)
Key Differences
Can IS 11169 (Part 1) 20C8GC Be Substituted With IS 11169 (Part 1) 20Ni2Cr2Mo3?
IS 11169 (Part 1) 20C8GC and IS 11169 (Part 1) 20Ni2Cr2Mo3 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
IS 11169 (Part 1) 20C8GC
0 active listings and RFQs →
IS 11169 (Part 1) 20Ni2Cr2Mo3
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 1) 20C8GC and IS 11169 (Part 1) 20Ni2Cr2Mo3?
Different category: IS 11169 (Part 1) 20C8GC is Carbon Steel, IS 11169 (Part 1) 20Ni2Cr2Mo3 is Alloy Steel. IS 11169 (Part 1) 20C8GC specifies Al which is not specified for IS 11169 (Part 1) 20Ni2Cr2Mo3.
Can IS 11169 (Part 1) 20C8GC be substituted with IS 11169 (Part 1) 20Ni2Cr2Mo3?
IS 11169 (Part 1) 20C8GC and IS 11169 (Part 1) 20Ni2Cr2Mo3 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.