IS 11169 (Part 1) 4C2 vs BS 970 (Part 1) 655M13

Related Material — 65% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 1) 4C2 (IS 11169 (Part 1):2022) and BS 970 (Part 1) 655M13 (BS 970 (Part 1):1991) are both steel grades. IS 11169 (Part 1) 4C2 is classified under Carbon Steel, while BS 970 (Part 1) 655M13 is classified under Alloy Steel — a different category, which is worth noting alongside the chemistry match below. IS 11169 (Part 1) 4C2 is typically used for cold heading and cold extrusion of parts not heat treated after cold forming; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, annex a), while BS 970 (Part 1) 655M13 is commonly used for case hardened gears, heavily loaded shafts. IS 11169 (Part 1) 4C2 is defined under Bureau of Indian Standards (IS), originating from India, while BS 970 (Part 1) 655M13 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, IS 11169 (Part 1) 4C2 vs BS 970 (Part 1) 655M13 is a 65.4% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 65%.

Frequently Compared With IS 11169 (Part 1) 4C2:
BS 970 (Part 3) 070M55 BS 970 (Part 1) 040A10 BS 970 (Part 1) 045M10 BS 970 (Part 3) 045M10 BS 970 (Part 1) 055M15 BS 970 (Part 1) 045A10 BS 970 (Part 1) 045A10 BS 970 (Part 1) 040A04 BS 970 (Part 3) 045A10 BS 970 (Part 1) 060A32 BS 970 (Part 1) 040A12 BS 970 (Part 1) 045M10
Match Breakdown
CHEMISTRY MATCH
65.4%
MECHANICAL MATCH
No shared data
OVERALL
65%
Specifications
Property IS 11169 (Part 1) 4C2 BS 970 (Part 1) 655M13
Standard IS 11169 (Part 1):2022 BS 970 (Part 1):1991
Category Carbon Steel Alloy Steel
C (%) <=0.08 0.10-0.16
Cr (%) <=0.15 0.70-1.00
Cu (%) <=0.15 Not specified
Mn (%) <=0.40 0.35-0.60
Mo (%) <=0.05 Not specified
Ni (%) <=0.15 3.00-3.75
P (%) <=0.035 Not specified
S (%) <=0.035 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 1) 4C2 BS 970 (Part 1) 655M13
Hardness, annealed (+AC) <=120 HBW Not specified
Condition Not specified Case hardened, 19 mm test bar
Tensile Strength Not specified 1000 MPa min
Elongation Not specified 9 % min
Typical Applications
IS 11169 (Part 1) 4C2
Cold heading and cold extrusion of parts not heat treated after cold forming; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, Annex A)
BS 970 (Part 1) 655M13
Case hardened gears, heavily loaded shafts
Key Differences
Can IS 11169 (Part 1) 4C2 Be Substituted With BS 970 (Part 1) 655M13?
IS 11169 (Part 1) 4C2 and BS 970 (Part 1) 655M13 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 11169 (Part 1) 4C2
No active listings currently.
BS 970 (Part 1) 655M13
Round Bar → (2 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 4200–6300 mm (165.35–248.03 in)
On M-EX Right Now
IS 11169 (Part 1) 4C2
0 active listings and RFQs →
BS 970 (Part 1) 655M13
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 1) 4C2 and BS 970 (Part 1) 655M13?
Different category: IS 11169 (Part 1) 4C2 is Carbon Steel, BS 970 (Part 1) 655M13 is Alloy Steel. IS 11169 (Part 1) 4C2 specifies Cu, Mo, P, S which are not specified for BS 970 (Part 1) 655M13.
Can IS 11169 (Part 1) 4C2 be substituted with BS 970 (Part 1) 655M13?
IS 11169 (Part 1) 4C2 and BS 970 (Part 1) 655M13 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.