IS 11169 (Part 2) X02Cr17Ni12Mo2 vs GB/T 3280 06Cr19Ni10

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 2) X02Cr17Ni12Mo2 (IS 11169 (Part 2):1989) and GB/T 3280 06Cr19Ni10 (GB/T 3280-2015) are both steel grades. Both fall under the Stainless Steel category. IS 11169 (Part 2) X02Cr17Ni12Mo2 is typically used for cold heading and cold extrusion; the standard covers wires, wire rods and bars (clause 1.1), while GB/T 3280 06Cr19Ni10 is commonly used for used for kitchen equipment, food processing machinery, chemical tanks, piping, architectural panels, and fasteners.. IS 11169 (Part 2) X02Cr17Ni12Mo2 is defined under Bureau of Indian Standards (IS), originating from India, while GB/T 3280 06Cr19Ni10 is defined under Guobiao Standards (GB/T), originating from China.

As per chemical composition, IS 11169 (Part 2) X02Cr17Ni12Mo2 vs GB/T 3280 06Cr19Ni10 is a 71.2% match. As per mechanical properties, the match is 26.7%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With IS 11169 (Part 2) X02Cr17Ni12Mo2:
ASTM A959 29-4C ASTM A959 .- GOST 5632 08X18H10 EN 10088-1 1.4301 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
71.2%
MECHANICAL MATCH
26.7%
OVERALL
35%
Specifications
Property IS 11169 (Part 2) X02Cr17Ni12Mo2 GB/T 3280 06Cr19Ni10
Standard IS 11169 (Part 2):1989 GB/T 3280-2015
Category Stainless Steel Stainless Steel
C (%) <=0.030 0.08 max
Si (%) <=1.0 1.00 max
Mn (%) <=2.0 2.00 max
Ni (%) 10.0-14.0 8.00-11.00
Cr (%) 16.0-18.0 18.00-20.00
Mo (%) 2.0-3.0 Not specified
S (%) <=0.030 0.030 max
P (%) <=0.045 0.045 max
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 2) X02Cr17Ni12Mo2 GB/T 3280 06Cr19Ni10
Yield Strength (0.2% proof) >=225 MPa Not specified
Tensile Strength 500-750 MPa 520-720 MPa
Elongation >=40% 40-60%
Impact (U-notch 5 mm) >=60 J Not specified
Condition Quenched reference test piece (Table 6 treatment) Not specified
Yield Strength Not specified 205-310 MPa
Hardness Not specified 187 HB max
Typical Applications
IS 11169 (Part 2) X02Cr17Ni12Mo2
Cold heading and cold extrusion; the standard covers wires, wire rods and bars (clause 1.1)
GB/T 3280 06Cr19Ni10
Used for kitchen equipment, food processing machinery, chemical tanks, piping, architectural panels, and fasteners.
Key Differences
Can IS 11169 (Part 2) X02Cr17Ni12Mo2 Be Substituted With GB/T 3280 06Cr19Ni10?
IS 11169 (Part 2) X02Cr17Ni12Mo2 and GB/T 3280 06Cr19Ni10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 11169 (Part 2) X02Cr17Ni12Mo2
No active listings currently.
GB/T 3280 06Cr19Ni10
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2900–3300 mm (114.17–129.92 in)
On M-EX Right Now
IS 11169 (Part 2) X02Cr17Ni12Mo2
0 active listings and RFQs →
GB/T 3280 06Cr19Ni10
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 2) X02Cr17Ni12Mo2 and GB/T 3280 06Cr19Ni10?
IS 11169 (Part 2) X02Cr17Ni12Mo2 specifies Mo which is not specified for GB/T 3280 06Cr19Ni10.
Can IS 11169 (Part 2) X02Cr17Ni12Mo2 be substituted with GB/T 3280 06Cr19Ni10?
IS 11169 (Part 2) X02Cr17Ni12Mo2 and GB/T 3280 06Cr19Ni10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.