IS 11169 (Part 2) X02Cr17Ni12Mo2 vs ASTM A959 .-

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 2) X02Cr17Ni12Mo2 (IS 11169 (Part 2):1989) and ASTM A959 .- (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. IS 11169 (Part 2) X02Cr17Ni12Mo2 is typically used for cold heading and cold extrusion; the standard covers wires, wire rods and bars (clause 1.1), while ASTM A959 .- is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). IS 11169 (Part 2) X02Cr17Ni12Mo2 is defined under Bureau of Indian Standards (IS), originating from India, while ASTM A959 .- is defined under ASTM International, originating from United States.

As per chemical composition, IS 11169 (Part 2) X02Cr17Ni12Mo2 vs ASTM A959 .- is a 64.1% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With IS 11169 (Part 2) X02Cr17Ni12Mo2:
ASTM A959 29-4C GB/T 3280 06Cr19Ni10 EN 10088-1 1.4301 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoVH GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
64.1%
MECHANICAL MATCH
No shared data
OVERALL
35%
Specifications
Property IS 11169 (Part 2) X02Cr17Ni12Mo2 ASTM A959 .-
Standard IS 11169 (Part 2):1989 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Si (%) <=1.0 <=1.00
Mn (%) <=2.0 <=1.00
Ni (%) 10.0-14.0 <=0.50
Cr (%) 16.0-18.0 18.0-20.0
Mo (%) 2.0-3.0 Not specified
S (%) <=0.030 <=0.030
P (%) <=0.045 <=0.040
Cb (%) Not specified 0.10-0.60
N (%) Not specified <=0.030
Ti (%) Not specified 0.07-0.30
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 2) X02Cr17Ni12Mo2 ASTM A959 .-
Yield Strength (0.2% proof) >=225 MPa Not specified
Tensile Strength 500-750 MPa Not specified
Elongation >=40% Not specified
Impact (U-notch 5 mm) >=60 J Not specified
Condition Quenched reference test piece (Table 6 treatment) Not specified
Typical Applications
IS 11169 (Part 2) X02Cr17Ni12Mo2
Cold heading and cold extrusion; the standard covers wires, wire rods and bars (clause 1.1)
ASTM A959 .-
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can IS 11169 (Part 2) X02Cr17Ni12Mo2 Be Substituted With ASTM A959 .-?
IS 11169 (Part 2) X02Cr17Ni12Mo2 and ASTM A959 .- share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
IS 11169 (Part 2) X02Cr17Ni12Mo2
0 active listings and RFQs →
ASTM A959 .-
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 2) X02Cr17Ni12Mo2 and ASTM A959 .-?
IS 11169 (Part 2) X02Cr17Ni12Mo2 specifies Mo which is not specified for ASTM A959 .-. ASTM A959 .- specifies Cb, N, Ti which are not specified for IS 11169 (Part 2) X02Cr17Ni12Mo2.
Can IS 11169 (Part 2) X02Cr17Ni12Mo2 be substituted with ASTM A959 .-?
IS 11169 (Part 2) X02Cr17Ni12Mo2 and ASTM A959 .- share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.