IS 11169 (Part 2) X04Cr19Ni10 vs GB/T 3280 06Cr19Ni10
Related Material — 69% match
based on chemical composition and mechanical property overlap.
IS 11169 (Part 2) X04Cr19Ni10 (IS 11169 (Part 2):1989) and GB/T 3280 06Cr19Ni10 (GB/T 3280-2015) are both steel grades.
Both fall under the Stainless Steel category.
IS 11169 (Part 2) X04Cr19Ni10 is typically used for cold heading and cold extrusion; the standard covers wires, wire rods and bars (clause 1.1), while GB/T 3280 06Cr19Ni10 is commonly used for used for kitchen equipment, food processing machinery, chemical tanks, piping, architectural panels, and fasteners..
IS 11169 (Part 2) X04Cr19Ni10 is defined under Bureau of Indian Standards (IS), originating from India, while GB/T 3280 06Cr19Ni10 is defined under Guobiao Standards (GB/T), originating from China.
As per chemical composition, IS 11169 (Part 2) X04Cr19Ni10 vs GB/T 3280 06Cr19Ni10 is a 89.9% match.
As per mechanical properties, the match is 27.3%.
Combined, this makes them a related material overall at 69%.
Frequently Compared With IS 11169 (Part 2) X04Cr19Ni10:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 11169 (Part 2) X04Cr19Ni10
GB/T 3280 06Cr19Ni10
Yield Strength (0.2% proof)
>=185 MPa
Not specified
Tensile Strength
500-700 MPa
520-720 MPa
Elongation
>=50%
40-60%
Impact (U-notch 5 mm)
>=60 J
Not specified
Condition
Quenched reference test piece (Table 6 treatment)
Not specified
Yield Strength
Not specified
205-310 MPa
Hardness
Not specified
187 HB max
Typical Applications
IS 11169 (Part 2) X04Cr19Ni10
Cold heading and cold extrusion; the standard covers wires, wire rods and bars (clause 1.1)
GB/T 3280 06Cr19Ni10
Used for kitchen equipment, food processing machinery, chemical tanks, piping, architectural panels, and fasteners.
Can IS 11169 (Part 2) X04Cr19Ni10 Be Substituted With GB/T 3280 06Cr19Ni10?
IS 11169 (Part 2) X04Cr19Ni10 and GB/T 3280 06Cr19Ni10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between IS 11169 (Part 2) X04Cr19Ni10 and GB/T 3280 06Cr19Ni10?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 11169 (Part 2) X04Cr19Ni10 be substituted with GB/T 3280 06Cr19Ni10?
IS 11169 (Part 2) X04Cr19Ni10 and GB/T 3280 06Cr19Ni10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.