IS 11169 (Part 2) X02Cr17Ni11Cu3Mo2 vs EN 10088-1 X2CrNiMoCuS17-10-2

Close Alternative — 82.6% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 2) X02Cr17Ni11Cu3Mo2 (IS 11169 (Part 2):2023) and EN 10088-1 X2CrNiMoCuS17-10-2 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. IS 11169 (Part 2) X02Cr17Ni11Cu3Mo2 is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 X2CrNiMoCuS17-10-2 is defined under European Standard (EN), originating from Europe.

As per chemical composition, IS 11169 (Part 2) X02Cr17Ni11Cu3Mo2 vs EN 10088-1 X2CrNiMoCuS17-10-2 is a 82.6% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 82.6%.

Frequently Compared With IS 11169 (Part 2) X02Cr17Ni11Cu3Mo2:
GOST 5632 08X18H10 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
82.6%
MECHANICAL MATCH
No shared data
OVERALL
82.6%
Specifications
Property IS 11169 (Part 2) X02Cr17Ni11Cu3Mo2 EN 10088-1 X2CrNiMoCuS17-10-2
Standard IS 11169 (Part 2):2023 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.04 <=0.030
Cr (%) 16.5-17.5 16.5-18.5
Cu (%) 3.00-3.50 1.30-1.80
Mn (%) <=2.00 <=2.00
Mo (%) 2.00-2.50 2.00-2.50
N (%) <=0.10 <=0.10
Ni (%) 10.0-11.0 10.0-13.0
P (%) <=0.045 <=0.045
S (%) <=0.015 0.10-0.20
Si (%) <=1.00 <=1.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 2) X02Cr17Ni11Cu3Mo2 EN 10088-1 X2CrNiMoCuS17-10-2
Reduction of Area, solution annealed (+AT) >=68% (over 5 to 50 mm) Not specified
Tensile Strength, solution annealed (+AT) <=610 MPa (over 5 to 50 mm) Not specified
Typical Applications
IS 11169 (Part 2) X02Cr17Ni11Cu3Mo2
Cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, Table 11)
EN 10088-1 X2CrNiMoCuS17-10-2
Not documented
Can IS 11169 (Part 2) X02Cr17Ni11Cu3Mo2 Be Substituted With EN 10088-1 X2CrNiMoCuS17-10-2?
IS 11169 (Part 2) X02Cr17Ni11Cu3Mo2 and EN 10088-1 X2CrNiMoCuS17-10-2 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
IS 11169 (Part 2) X02Cr17Ni11Cu3Mo2
0 active listings and RFQs →
EN 10088-1 X2CrNiMoCuS17-10-2
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 2) X02Cr17Ni11Cu3Mo2 and EN 10088-1 X2CrNiMoCuS17-10-2?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 11169 (Part 2) X02Cr17Ni11Cu3Mo2 be substituted with EN 10088-1 X2CrNiMoCuS17-10-2?
IS 11169 (Part 2) X02Cr17Ni11Cu3Mo2 and EN 10088-1 X2CrNiMoCuS17-10-2 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.