IS 11169 (Part 2) X02Cr17Ni12Mo3N vs EN 10088-1 X2CrNiMoN17-11-2

Strong Match — 86.3% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 2) X02Cr17Ni12Mo3N (IS 11169 (Part 2):2023) and EN 10088-1 X2CrNiMoN17-11-2 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. IS 11169 (Part 2) X02Cr17Ni12Mo3N is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 X2CrNiMoN17-11-2 is defined under European Standard (EN), originating from Europe.

As per chemical composition, IS 11169 (Part 2) X02Cr17Ni12Mo3N vs EN 10088-1 X2CrNiMoN17-11-2 is a 86.3% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 86.3%.

Frequently Compared With IS 11169 (Part 2) X02Cr17Ni12Mo3N:
EN 10088-1 1.4845 GOST 5632 12Kh13 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo GB/T 3280 06Cr19Ni10
Match Breakdown
CHEMISTRY MATCH
86.3%
MECHANICAL MATCH
No shared data
OVERALL
86.3%
Specifications
Property IS 11169 (Part 2) X02Cr17Ni12Mo3N EN 10088-1 X2CrNiMoN17-11-2
Standard IS 11169 (Part 2):2023 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Cr (%) 16.5-18.5 16.5-18.5
Cu (%) <=1.00 Not specified
Mn (%) <=2.00 <=2.00
Mo (%) 2.50-3.00 2.00-2.50
N (%) 0.12-0.22 0.12-0.22
Ni (%) 10.5-13.0 10.0-12.5
P (%) <=0.045 <=0.045
S (%) <=0.015 <=0.015
Si (%) <=1.00 <=1.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 2) X02Cr17Ni12Mo3N EN 10088-1 X2CrNiMoN17-11-2
Reduction of Area, solution annealed (+AT) >=60% (over 5 to 50 mm) Not specified
Tensile Strength, solution annealed (+AT) <=780 MPa (over 5 to 50 mm) Not specified
Typical Applications
IS 11169 (Part 2) X02Cr17Ni12Mo3N
Cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, Table 11)
EN 10088-1 X2CrNiMoN17-11-2
Not documented
Key Differences
Can IS 11169 (Part 2) X02Cr17Ni12Mo3N Be Substituted With EN 10088-1 X2CrNiMoN17-11-2?
IS 11169 (Part 2) X02Cr17Ni12Mo3N and EN 10088-1 X2CrNiMoN17-11-2 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X2CrNiMoN17-11-2 is often considered as a substitute for IS 11169 (Part 2) X02Cr17Ni12Mo3N in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 11169 (Part 2) X02Cr17Ni12Mo3N
0 active listings and RFQs →
EN 10088-1 X2CrNiMoN17-11-2
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 2) X02Cr17Ni12Mo3N and EN 10088-1 X2CrNiMoN17-11-2?
IS 11169 (Part 2) X02Cr17Ni12Mo3N specifies Cu which is not specified for EN 10088-1 X2CrNiMoN17-11-2.
Can IS 11169 (Part 2) X02Cr17Ni12Mo3N be substituted with EN 10088-1 X2CrNiMoN17-11-2?
IS 11169 (Part 2) X02Cr17Ni12Mo3N and EN 10088-1 X2CrNiMoN17-11-2 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X2CrNiMoN17-11-2 is often considered as a substitute for IS 11169 (Part 2) X02Cr17Ni12Mo3N in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.