IS 11169 (Part 2) X02Cr18Ni8Cu vs ASTM A959 S30430

Close Alternative — 79.4% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 2) X02Cr18Ni8Cu (IS 11169 (Part 2):2023) and ASTM A959 S30430 (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. IS 11169 (Part 2) X02Cr18Ni8Cu is typically used for cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, table 11), while ASTM A959 S30430 is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). IS 11169 (Part 2) X02Cr18Ni8Cu is defined under Bureau of Indian Standards (IS), originating from India, while ASTM A959 S30430 is defined under ASTM International, originating from United States.

As per chemical composition, IS 11169 (Part 2) X02Cr18Ni8Cu vs ASTM A959 S30430 is a 79.4% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 79.4%.

Frequently Compared With IS 11169 (Part 2) X02Cr18Ni8Cu:
EN 10088-1 1.4301 ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
79.4%
MECHANICAL MATCH
No shared data
OVERALL
79.4%
Specifications
Property IS 11169 (Part 2) X02Cr18Ni8Cu ASTM A959 S30430
Standard IS 11169 (Part 2):2023 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.035 <=0.03
Cr (%) 18.0-19.0 17.0-19.0
Cu (%) 1.50-2.00 3.0-4.0
Mn (%) 1.50-2.00 <=2.00
N (%) <=0.10 Not specified
Ni (%) 8.0-9.0 8.0-10.0
P (%) <=0.045 <=0.045
S (%) <=0.015 <=0.030
Si (%) <=1.00 <=1.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 2) X02Cr18Ni8Cu ASTM A959 S30430
Reduction of Area, solution annealed (+AT) >=68% (over 5 to 50 mm) Not specified
Tensile Strength, solution annealed (+AT) <=610 MPa (over 5 to 50 mm) Not specified
Typical Applications
IS 11169 (Part 2) X02Cr18Ni8Cu
Cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, Table 11)
ASTM A959 S30430
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can IS 11169 (Part 2) X02Cr18Ni8Cu Be Substituted With ASTM A959 S30430?
IS 11169 (Part 2) X02Cr18Ni8Cu and ASTM A959 S30430 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
IS 11169 (Part 2) X02Cr18Ni8Cu
0 active listings and RFQs →
ASTM A959 S30430
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 2) X02Cr18Ni8Cu and ASTM A959 S30430?
IS 11169 (Part 2) X02Cr18Ni8Cu specifies N which is not specified for ASTM A959 S30430.
Can IS 11169 (Part 2) X02Cr18Ni8Cu be substituted with ASTM A959 S30430?
IS 11169 (Part 2) X02Cr18Ni8Cu and ASTM A959 S30430 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.