IS 11169 (Part 2) X02Cr22Ni5Mo3N vs ASTM A959 S31803

Strong Match — 98% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 2) X02Cr22Ni5Mo3N (IS 11169 (Part 2):2023) and ASTM A959 S31803 (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. IS 11169 (Part 2) X02Cr22Ni5Mo3N is typically used for cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 2 to 25 mm (clause 1.1, table 12), while ASTM A959 S31803 is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). IS 11169 (Part 2) X02Cr22Ni5Mo3N is defined under Bureau of Indian Standards (IS), originating from India, while ASTM A959 S31803 is defined under ASTM International, originating from United States.

As per chemical composition, IS 11169 (Part 2) X02Cr22Ni5Mo3N vs ASTM A959 S31803 is a 98% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 98%.

Frequently Compared With IS 11169 (Part 2) X02Cr22Ni5Mo3N:
ASTM A959 2205 ASTM A959 2304 ASTM A959 255 GOST 5632 06Kh23N28 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoVH GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 EN 10088-1 1.4006 IS 1570 (Part 7) 11Cr17Ni13W3TiH
Match Breakdown
CHEMISTRY MATCH
98%
MECHANICAL MATCH
No shared data
OVERALL
98%
Specifications
Property IS 11169 (Part 2) X02Cr22Ni5Mo3N ASTM A959 S31803
Standard IS 11169 (Part 2):2023 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Cr (%) 21.0-23.0 21.0-23.0
Mn (%) <=2.00 <=2.00
Mo (%) 2.50-3.50 2.5-3.5
N (%) 0.10-0.2 0.08-0.20
Ni (%) 4.5-6.5 4.5-6.5
P (%) <=0.035 <=0.030
S (%) <=0.015 <=0.020
Si (%) <=1.00 <=1.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 2) X02Cr22Ni5Mo3N ASTM A959 S31803
Reduction of Area, solution annealed (+AT) >=55% (over 2 to 25 mm) Not specified
Tensile Strength, solution annealed (+AT) <=880 MPa (over 2 to 25 mm) Not specified
Typical Applications
IS 11169 (Part 2) X02Cr22Ni5Mo3N
Cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 2 to 25 mm (clause 1.1, Table 12)
ASTM A959 S31803
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Can IS 11169 (Part 2) X02Cr22Ni5Mo3N Be Substituted With ASTM A959 S31803?
IS 11169 (Part 2) X02Cr22Ni5Mo3N and ASTM A959 S31803 overlap closely enough on chemistry and mechanical properties that ASTM A959 S31803 is often considered as a substitute for IS 11169 (Part 2) X02Cr22Ni5Mo3N in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 11169 (Part 2) X02Cr22Ni5Mo3N
0 active listings and RFQs →
ASTM A959 S31803
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 2) X02Cr22Ni5Mo3N and ASTM A959 S31803?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 11169 (Part 2) X02Cr22Ni5Mo3N be substituted with ASTM A959 S31803?
IS 11169 (Part 2) X02Cr22Ni5Mo3N and ASTM A959 S31803 overlap closely enough on chemistry and mechanical properties that ASTM A959 S31803 is often considered as a substitute for IS 11169 (Part 2) X02Cr22Ni5Mo3N in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.