IS 11169 (Part 2) X02Cr22Ni5Mo3N vs EN 10088-1 X2CrNiMoN25-7-4

Close Alternative — 72.7% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 2) X02Cr22Ni5Mo3N (IS 11169 (Part 2):2023) and EN 10088-1 X2CrNiMoN25-7-4 (EN 10088-1:2023) are both steel grades. Both fall under the Stainless Steel category. IS 11169 (Part 2) X02Cr22Ni5Mo3N is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 X2CrNiMoN25-7-4 is defined under European Standard (EN), originating from Europe.

As per chemical composition, IS 11169 (Part 2) X02Cr22Ni5Mo3N vs EN 10088-1 X2CrNiMoN25-7-4 is a 72.7% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 72.7%.

Frequently Compared With IS 11169 (Part 2) X02Cr22Ni5Mo3N:
ASTM A959 2205 ASTM A959 2304 ASTM A959 255 GOST 5632 06Kh23N28 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 EN 10088-1 1.4006 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
72.7%
MECHANICAL MATCH
No shared data
OVERALL
72.7%
Specifications
Property IS 11169 (Part 2) X02Cr22Ni5Mo3N EN 10088-1 X2CrNiMoN25-7-4
Standard IS 11169 (Part 2):2023 EN 10088-1:2023
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Cr (%) 21.0-23.0 24.0-26.0
Mn (%) <=2.00 <=2.00
Mo (%) 2.50-3.50 3.00-4.5
N (%) 0.10-0.2 0.24-0.35
Ni (%) 4.5-6.5 6.0-8.0
P (%) <=0.035 <=0.035
S (%) <=0.015 <=0.015
Si (%) <=1.00 <=1.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 2) X02Cr22Ni5Mo3N EN 10088-1 X2CrNiMoN25-7-4
Reduction of Area, solution annealed (+AT) >=55% (over 2 to 25 mm) Not specified
Tensile Strength, solution annealed (+AT) <=880 MPa (over 2 to 25 mm) Not specified
Typical Applications
IS 11169 (Part 2) X02Cr22Ni5Mo3N
Cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 2 to 25 mm (clause 1.1, Table 12)
EN 10088-1 X2CrNiMoN25-7-4
Not documented
Can IS 11169 (Part 2) X02Cr22Ni5Mo3N Be Substituted With EN 10088-1 X2CrNiMoN25-7-4?
IS 11169 (Part 2) X02Cr22Ni5Mo3N and EN 10088-1 X2CrNiMoN25-7-4 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
IS 11169 (Part 2) X02Cr22Ni5Mo3N
0 active listings and RFQs →
EN 10088-1 X2CrNiMoN25-7-4
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 2) X02Cr22Ni5Mo3N and EN 10088-1 X2CrNiMoN25-7-4?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 11169 (Part 2) X02Cr22Ni5Mo3N be substituted with EN 10088-1 X2CrNiMoN25-7-4?
IS 11169 (Part 2) X02Cr22Ni5Mo3N and EN 10088-1 X2CrNiMoN25-7-4 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.