IS 11169 (Part 2) X02Ni18Cr16 vs GOST 5632 06Kh23N28
Minimal Match — 46.4% match
based on chemical composition and mechanical property overlap.
IS 11169 (Part 2) X02Ni18Cr16 (IS 11169 (Part 2):2023) and GOST 5632 06Kh23N28 (GOST 5632-2014) are both steel grades.
Both fall under the Stainless Steel category.
IS 11169 (Part 2) X02Ni18Cr16 is typically used for cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, table 11), while GOST 5632 06Kh23N28 is commonly used for furnace components, heat exchangers, high temperature applications.
IS 11169 (Part 2) X02Ni18Cr16 is defined under Bureau of Indian Standards (IS) (India).
As per chemical composition, IS 11169 (Part 2) X02Ni18Cr16 vs GOST 5632 06Kh23N28 is a 69.6% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 46.4%.
Frequently Compared With IS 11169 (Part 2) X02Ni18Cr16:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 11169 (Part 2) X02Ni18Cr16
GOST 5632 06Kh23N28
Reduction of Area, cold drawn and solution annealed (+AT+C+AT)
>=68% (0.8 to 5 mm)
Not specified
Tensile Strength, cold drawn and solution annealed (+AT+C+AT)
<=640 MPa (0.8 to 2 mm) / <=600 MPa (over 2 to 5 mm)
Not specified
Tensile Strength
Not specified
≥510 MPa
Yield Strength
Not specified
≥196 MPa
Elongation
Not specified
≥35%
Max Service Temp
Not specified
1050°C
Typical Applications
IS 11169 (Part 2) X02Ni18Cr16
Cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, Table 11)
GOST 5632 06Kh23N28
Furnace components, heat exchangers, high temperature applications
Key Differences
IS 11169 (Part 2) X02Ni18Cr16 specifies P, S which are not specified for GOST 5632 06Kh23N28.
Can IS 11169 (Part 2) X02Ni18Cr16 Be Substituted With GOST 5632 06Kh23N28?
IS 11169 (Part 2) X02Ni18Cr16 and GOST 5632 06Kh23N28 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between IS 11169 (Part 2) X02Ni18Cr16 and GOST 5632 06Kh23N28?
IS 11169 (Part 2) X02Ni18Cr16 specifies P, S which are not specified for GOST 5632 06Kh23N28.
Can IS 11169 (Part 2) X02Ni18Cr16 be substituted with GOST 5632 06Kh23N28?
IS 11169 (Part 2) X02Ni18Cr16 and GOST 5632 06Kh23N28 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.