IS 11169 (Part 2) X02Ni18Cr16 vs ASTM A959 .-

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 2) X02Ni18Cr16 (IS 11169 (Part 2):2023) and ASTM A959 .- (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. IS 11169 (Part 2) X02Ni18Cr16 is typically used for cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, table 11), while ASTM A959 .- is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). IS 11169 (Part 2) X02Ni18Cr16 is defined under Bureau of Indian Standards (IS), originating from India, while ASTM A959 .- is defined under ASTM International, originating from United States.

As per chemical composition, IS 11169 (Part 2) X02Ni18Cr16 vs ASTM A959 .- is a 70.4% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With IS 11169 (Part 2) X02Ni18Cr16:
EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr13H GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
70.4%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property IS 11169 (Part 2) X02Ni18Cr16 ASTM A959 .-
Standard IS 11169 (Part 2):2023 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.04 <=0.030
Cr (%) 15.0-17.0 18.0-20.0
Mn (%) <=2.00 <=1.00
Ni (%) 17.0-19.0 <=0.50
P (%) <=0.045 <=0.040
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
Cb (%) Not specified 0.10-0.60
N (%) Not specified <=0.030
Ti (%) Not specified 0.07-0.30
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 2) X02Ni18Cr16 ASTM A959 .-
Reduction of Area, cold drawn and solution annealed (+AT+C+AT) >=68% (0.8 to 5 mm) Not specified
Tensile Strength, cold drawn and solution annealed (+AT+C+AT) <=640 MPa (0.8 to 2 mm) / <=600 MPa (over 2 to 5 mm) Not specified
Typical Applications
IS 11169 (Part 2) X02Ni18Cr16
Cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, Table 11)
ASTM A959 .-
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can IS 11169 (Part 2) X02Ni18Cr16 Be Substituted With ASTM A959 .-?
IS 11169 (Part 2) X02Ni18Cr16 and ASTM A959 .- share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
IS 11169 (Part 2) X02Ni18Cr16
0 active listings and RFQs →
ASTM A959 .-
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 2) X02Ni18Cr16 and ASTM A959 .-?
ASTM A959 .- specifies Cb, N, Ti which are not specified for IS 11169 (Part 2) X02Ni18Cr16.
Can IS 11169 (Part 2) X02Ni18Cr16 be substituted with ASTM A959 .-?
IS 11169 (Part 2) X02Ni18Cr16 and ASTM A959 .- share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.