Minimal Match — 35% match
based on chemical composition and mechanical property overlap.
IS 11169 (Part 2) X04Cr17 (IS 11169 (Part 2):2023) and GB/T 3280 06Cr19Ni10 (GB/T 3280-2015) are both steel grades.
Both fall under the Stainless Steel category.
IS 11169 (Part 2) X04Cr17 is typically used for cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 25 mm (clause 1.1, table 13), while GB/T 3280 06Cr19Ni10 is commonly used for used for kitchen equipment, food processing machinery, chemical tanks, piping, architectural panels, and fasteners..
IS 11169 (Part 2) X04Cr17 is defined under Bureau of Indian Standards (IS), originating from India, while GB/T 3280 06Cr19Ni10 is defined under Guobiao Standards (GB/T), originating from China.
As per chemical composition, IS 11169 (Part 2) X04Cr17 vs GB/T 3280 06Cr19Ni10 is a 80.2% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 35%.
Frequently Compared With IS 11169 (Part 2) X04Cr17:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 11169 (Part 2) X04Cr17
GB/T 3280 06Cr19Ni10
Reduction of Area, soft annealed (+A)
>=63% (over 5 to 25 mm)
Not specified
Tensile Strength, soft annealed (+A)
<=560 MPa (over 5 to 25 mm)
Not specified
Tensile Strength
Not specified
520-720 MPa
Yield Strength
Not specified
205-310 MPa
Elongation
Not specified
40-60%
Hardness
Not specified
187 HB max
Typical Applications
IS 11169 (Part 2) X04Cr17
Cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 25 mm (clause 1.1, Table 13)
GB/T 3280 06Cr19Ni10
Used for kitchen equipment, food processing machinery, chemical tanks, piping, architectural panels, and fasteners.
Key Differences
GB/T 3280 06Cr19Ni10 specifies Ni which is not specified for IS 11169 (Part 2) X04Cr17.
Can IS 11169 (Part 2) X04Cr17 Be Substituted With GB/T 3280 06Cr19Ni10?
IS 11169 (Part 2) X04Cr17 and GB/T 3280 06Cr19Ni10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between IS 11169 (Part 2) X04Cr17 and GB/T 3280 06Cr19Ni10?
GB/T 3280 06Cr19Ni10 specifies Ni which is not specified for IS 11169 (Part 2) X04Cr17.
Can IS 11169 (Part 2) X04Cr17 be substituted with GB/T 3280 06Cr19Ni10?
IS 11169 (Part 2) X04Cr17 and GB/T 3280 06Cr19Ni10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.