IS 11169 (Part 2) X04Cr17 (IS 11169 (Part 2):2023) and GOST 5632 08X18H10 (GOST 5632-2014) are both steel grades.
Both fall under the Stainless Steel category.
IS 11169 (Part 2) X04Cr17 is typically used for cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 25 mm (clause 1.1, table 13), while GOST 5632 08X18H10 is commonly used for chemical equipment, food processing, general corrosion resistant applications.
IS 11169 (Part 2) X04Cr17 is defined under Bureau of Indian Standards (IS) (India).
As per chemical composition, IS 11169 (Part 2) X04Cr17 vs GOST 5632 08X18H10 is a 70.8% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 35%.
Frequently Compared With IS 11169 (Part 2) X04Cr17:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 11169 (Part 2) X04Cr17
GOST 5632 08X18H10
Reduction of Area, soft annealed (+A)
>=63% (over 5 to 25 mm)
Not specified
Tensile Strength, soft annealed (+A)
<=560 MPa (over 5 to 25 mm)
Not specified
Tensile Strength
Not specified
≥520 MPa
Yield Strength
Not specified
≥205 MPa
Elongation
Not specified
≥40%
Typical Applications
IS 11169 (Part 2) X04Cr17
Cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 25 mm (clause 1.1, Table 13)
GOST 5632 08X18H10
Chemical equipment, food processing, general corrosion resistant applications
Key Differences
GOST 5632 08X18H10 specifies Ni which is not specified for IS 11169 (Part 2) X04Cr17.
Can IS 11169 (Part 2) X04Cr17 Be Substituted With GOST 5632 08X18H10?
IS 11169 (Part 2) X04Cr17 and GOST 5632 08X18H10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between IS 11169 (Part 2) X04Cr17 and GOST 5632 08X18H10?
GOST 5632 08X18H10 specifies Ni which is not specified for IS 11169 (Part 2) X04Cr17.
Can IS 11169 (Part 2) X04Cr17 be substituted with GOST 5632 08X18H10?
IS 11169 (Part 2) X04Cr17 and GOST 5632 08X18H10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.