IS 11169 (Part 2):2023 X04Cr17Ni12Mo2Ti Steel: Specifications, Equivalents & Listings

Category: Stainless Steel

Grade Details

Grade	IS 11169 (Part 2):2023 X04Cr17Ni12Mo2Ti
Standard	IS 11169 (Part 2):2023
Applications	Cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, Table 11)

Equivalent / Similar Grades

Grade	Standard	Region	Live on M-EX
ISO 4571-316-35-I	ISO 4954	International	Not yet on M-EX
UNS S31635	ASTM A959	USA	Not yet on M-EX
EN X6CrNiMoTi17-12-2 (1.4571)	EN 10263	Europe	Not yet on M-EX
JIS SUS316Ti	JIS	Japan	Not yet on M-EX
GB/ISC S31668	GB	China	Not yet on M-EX
IS 1570 (Part 5) X04Cr17Ni12Mo2Ti	IS 1570 (Part 5):1985	India	No activity yet
IS 11169 (Part 2) X04Cr17Ni12Mo2Ti	IS 11169 (Part 2):1989	India	No activity yet
IS 6911 X04Cr17Ni12Mo2Ti	IS 6911:1992	India	No activity yet
BS 970 (Part 3) 316S31	BS 970 (Part 3):1991	UK	No activity yet
BS 970 (Part 3) 320S31	BS 970 (Part 3):1991	UK	No activity yet
EN 10088-1 X6CrNiMoTi17-12-2	EN 10088-1:2014	Europe (CEN)	No activity yet
EN 10088-1 X6CrNiMoNb17-12-2	EN 10088-1:2014	Europe (CEN)	No activity yet

Grade ComparisonCompare With a Specific Grade →

Grade	Standard	Match
BS 970 (Part 3) 316S31	BS 970 (Part 3):1991	Strong Match
BS 970 (Part 1) 316S31	BS 970 (Part 1):1983	Strong Match
EN 10088-1 X6CrNiMoTi17-12-2	EN 10088-1:2014	Strong Match
EN 10088-1 X6CrNiMoNb17-12-2	EN 10088-1:2014	Strong Match
EN 10088-1 X6CrNiMoTi17-12-2	EN 10088-1:2023	Strong Match
EN 10088-1 X6CrNiMoNb17-12-2	EN 10088-1:2023	Strong Match
BS 970 (Part 3) 320S31	BS 970 (Part 3):1991	Strong Match
BS 970 (Part 1) 320S31	BS 970 (Part 1):1983	Strong Match

Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.

Chemical Composition (%)

C	Cr	Cu	Mn	Mo	Ni	P	S	Si	Ti
<=0.08	16.5-18.5	<=1.00	<=2.00	2.00-2.50	10.5-13.5	<=0.045	<=0.030	<=1.00	5xC-0.70

Mechanical Properties

Reduction of Area, solution annealed (+AT)	>=65% (over 5 to 50 mm)
Tensile Strength, solution annealed (+AT)	<=680 MPa (over 5 to 50 mm)

More data from IS 11169 (Part 2):2023

From the standard

Other composition limits from the table notes

Values

Maximum unless a range is given (ladle analysis)

Steel type

Austenitic with molybdenum

Titanium

5 times the carbon content up to 0.70 percent

Elements not listed are not added intentionally without the purchaser's agreement, except those used to finish the heat.

Source: IS 11169 (Part 2):2023, Table 10 and its notes

Tensile strength and reduction of area by delivery condition by delivery condition and size

Delivery condition	Diameter (mm)	Tensile strength, max (MPa)	Reduction of area, min (%)
+AT or +AT+PE	over 5 to 10	680	65
+AT or +AT+PE	over 10 to 25	680	65
+AT or +AT+PE	over 25 to 50	680	65
+AT+C	over 5 to 10	850	-
+AT+C	over 10 to 25	810	-
+AT+C+AT	over 2 to 5	720	65
+AT+C+AT	over 5 to 10	680	65
+AT+C+AT	over 10 to 25	680	65
+AT+C+AT+LC	over 2 to 5	770	60
+AT+C+AT+LC	over 5 to 10	730	60

Codes: +AT solution annealed, +A soft annealed, +PE peeled, +C cold drawn, +LC skin passed. Diameter ranges are over the first figure up to and including the second. No reduction of area is specified for +AT+C. For non-circular sections the properties are agreed between manufacturer and purchaser.

Source: IS 11169 (Part 2):2023, Table 11

Active IS 11169 (Part 2):2023 X04Cr17Ni12Mo2Ti Listings on M-EX (For Sale)

+ Create a Listing for this grade

No active IS 11169 (Part 2):2023 X04Cr17Ni12Mo2Ti listings at this time.

Buyer RFQs for IS 11169 (Part 2):2023 X04Cr17Ni12Mo2Ti

+ Post an RFQ for this grade

No open buyer requirements for IS 11169 (Part 2):2023 X04Cr17Ni12Mo2Ti at this time.

IS 11169 (Part 2):2023 X04Cr17Ni12Mo2Ti Steel: Specifications & Listings

More data from IS 11169 (Part 2):2023

Active IS 11169 (Part 2):2023 X04Cr17Ni12Mo2Ti Listings on M-EX (For Sale)

Buyer RFQs for IS 11169 (Part 2):2023 X04Cr17Ni12Mo2Ti