IS 11169 (Part 2) X04Cr17Ni12Mo2Ti vs GOST 5632 12Kh13
Minimal Match — 34.6% match
based on chemical composition and mechanical property overlap.
IS 11169 (Part 2) X04Cr17Ni12Mo2Ti (IS 11169 (Part 2):2023) and GOST 5632 12Kh13 (GOST 5632-2014) are both steel grades.
Both fall under the Stainless Steel category.
IS 11169 (Part 2) X04Cr17Ni12Mo2Ti is typically used for cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, table 11), while GOST 5632 12Kh13 is commonly used for turbine blades, pump shafts, fasteners, cutlery.
IS 11169 (Part 2) X04Cr17Ni12Mo2Ti is defined under Bureau of Indian Standards (IS) (India).
As per chemical composition, IS 11169 (Part 2) X04Cr17Ni12Mo2Ti vs GOST 5632 12Kh13 is a 51.9% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 34.6%.
Frequently Compared With IS 11169 (Part 2) X04Cr17Ni12Mo2Ti:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 11169 (Part 2) X04Cr17Ni12Mo2Ti
GOST 5632 12Kh13
Reduction of Area, solution annealed (+AT)
>=65% (over 5 to 50 mm)
Not specified
Tensile Strength, solution annealed (+AT)
<=680 MPa (over 5 to 50 mm)
Not specified
Tensile Strength
Not specified
≥540 MPa (annealed)
Hardness HRC
Not specified
36–45 (hardened)
Typical Applications
IS 11169 (Part 2) X04Cr17Ni12Mo2Ti
Cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, Table 11)
GOST 5632 12Kh13
Turbine blades, pump shafts, fasteners, cutlery
Key Differences
IS 11169 (Part 2) X04Cr17Ni12Mo2Ti specifies Cu, Mo, P, S which are not specified for GOST 5632 12Kh13.
Can IS 11169 (Part 2) X04Cr17Ni12Mo2Ti Be Substituted With GOST 5632 12Kh13?
IS 11169 (Part 2) X04Cr17Ni12Mo2Ti and GOST 5632 12Kh13 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between IS 11169 (Part 2) X04Cr17Ni12Mo2Ti and GOST 5632 12Kh13?
IS 11169 (Part 2) X04Cr17Ni12Mo2Ti specifies Cu, Mo, P, S which are not specified for GOST 5632 12Kh13.
Can IS 11169 (Part 2) X04Cr17Ni12Mo2Ti be substituted with GOST 5632 12Kh13?
IS 11169 (Part 2) X04Cr17Ni12Mo2Ti and GOST 5632 12Kh13 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.