IS 11169 (Part 2) X04Cr18Ni9Cu vs EN 10088-1 X8CrNiS18-9
Strong Match — 91.1% match
based on chemical composition and mechanical property overlap.
IS 11169 (Part 2) X04Cr18Ni9Cu (IS 11169 (Part 2):2023) and EN 10088-1 X8CrNiS18-9 (EN 10088-1:2014) are both steel grades.
Both fall under the Stainless Steel category.
IS 11169 (Part 2) X04Cr18Ni9Cu is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 X8CrNiS18-9 is defined under European Standard (EN), originating from Europe.
As per chemical composition, IS 11169 (Part 2) X04Cr18Ni9Cu vs EN 10088-1 X8CrNiS18-9 is a 91.1% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a strong match overall at 91.1%.
Frequently Compared With IS 11169 (Part 2) X04Cr18Ni9Cu:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 11169 (Part 2) X04Cr18Ni9Cu
EN 10088-1 X8CrNiS18-9
Reduction of Area, cold drawn and solution annealed (+AT+C+AT)
>=60% (0.8 to 5 mm) / >=65% (over 5 to 25 mm)
Not specified
Tensile Strength, cold drawn and solution annealed (+AT+C+AT)
<=710 MPa (0.8 to 2 mm) / <=700 MPa (over 2 to 5 mm) / <=650 MPa (over 5 to 25 mm)
Not specified
Typical Applications
IS 11169 (Part 2) X04Cr18Ni9Cu
Cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, Table 11)
EN 10088-1 X8CrNiS18-9
Not documented
Can IS 11169 (Part 2) X04Cr18Ni9Cu Be Substituted With EN 10088-1 X8CrNiS18-9?
IS 11169 (Part 2) X04Cr18Ni9Cu and EN 10088-1 X8CrNiS18-9 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X8CrNiS18-9 is often considered as a substitute for IS 11169 (Part 2) X04Cr18Ni9Cu in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between IS 11169 (Part 2) X04Cr18Ni9Cu and EN 10088-1 X8CrNiS18-9?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 11169 (Part 2) X04Cr18Ni9Cu be substituted with EN 10088-1 X8CrNiS18-9?
IS 11169 (Part 2) X04Cr18Ni9Cu and EN 10088-1 X8CrNiS18-9 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X8CrNiS18-9 is often considered as a substitute for IS 11169 (Part 2) X04Cr18Ni9Cu in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.