IS 11169 (Part 2) X04Cr18Ni9Cu vs EN 10088-1 X5CrNi18-10

Strong Match — 91.5% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 2) X04Cr18Ni9Cu (IS 11169 (Part 2):2023) and EN 10088-1 X5CrNi18-10 (EN 10088-1:2023) are both steel grades. Both fall under the Stainless Steel category. IS 11169 (Part 2) X04Cr18Ni9Cu is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 X5CrNi18-10 is defined under European Standard (EN), originating from Europe.

As per chemical composition, IS 11169 (Part 2) X04Cr18Ni9Cu vs EN 10088-1 X5CrNi18-10 is a 91.5% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 91.5%.

Frequently Compared With IS 11169 (Part 2) X04Cr18Ni9Cu:
GOST 5632 08X18H10 GOST 5632 12Kh13 EN 10088-1 1.4301 EN 10088-1 1.4845 EN 10088-1 1.4006 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
91.5%
MECHANICAL MATCH
No shared data
OVERALL
91.5%
Specifications
Property IS 11169 (Part 2) X04Cr18Ni9Cu EN 10088-1 X5CrNi18-10
Standard IS 11169 (Part 2):2023 EN 10088-1:2023
Category Stainless Steel Stainless Steel
C (%) <=0.08 <=0.07
Cr (%) 17.0-19.0 17.5-19.5
Cu (%) 1.00-3.00 Not specified
Mn (%) <=2.00 <=2.00
N (%) <=0.10 <=0.10
Ni (%) 8.0-10.5 8.0-10.5
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.015
Si (%) <=1.00 <=1.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 2) X04Cr18Ni9Cu EN 10088-1 X5CrNi18-10
Reduction of Area, cold drawn and solution annealed (+AT+C+AT) >=60% (0.8 to 5 mm) / >=65% (over 5 to 25 mm) Not specified
Tensile Strength, cold drawn and solution annealed (+AT+C+AT) <=710 MPa (0.8 to 2 mm) / <=700 MPa (over 2 to 5 mm) / <=650 MPa (over 5 to 25 mm) Not specified
Typical Applications
IS 11169 (Part 2) X04Cr18Ni9Cu
Cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, Table 11)
EN 10088-1 X5CrNi18-10
Not documented
Key Differences
Can IS 11169 (Part 2) X04Cr18Ni9Cu Be Substituted With EN 10088-1 X5CrNi18-10?
IS 11169 (Part 2) X04Cr18Ni9Cu and EN 10088-1 X5CrNi18-10 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X5CrNi18-10 is often considered as a substitute for IS 11169 (Part 2) X04Cr18Ni9Cu in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 11169 (Part 2) X04Cr18Ni9Cu
0 active listings and RFQs →
EN 10088-1 X5CrNi18-10
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 2) X04Cr18Ni9Cu and EN 10088-1 X5CrNi18-10?
IS 11169 (Part 2) X04Cr18Ni9Cu specifies Cu which is not specified for EN 10088-1 X5CrNi18-10.
Can IS 11169 (Part 2) X04Cr18Ni9Cu be substituted with EN 10088-1 X5CrNi18-10?
IS 11169 (Part 2) X04Cr18Ni9Cu and EN 10088-1 X5CrNi18-10 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X5CrNi18-10 is often considered as a substitute for IS 11169 (Part 2) X04Cr18Ni9Cu in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.