IS 11169 (Part 2) X12Cr13 vs BS 970 (Part 1) 410S21

Strong Match — 94.9% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 2) X12Cr13 (IS 11169 (Part 2):2023) and BS 970 (Part 1) 410S21 (BS 970 (Part 1):1983) are both steel grades. Both fall under the Stainless Steel category. IS 11169 (Part 2) X12Cr13 is typically used for cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 100 mm (clause 1.1, table 14), while BS 970 (Part 1) 410S21 is commonly used for stainless and heat resisting steel for mechanical and allied engineering purposes (table 13).. IS 11169 (Part 2) X12Cr13 is defined under Bureau of Indian Standards (IS), originating from India, while BS 970 (Part 1) 410S21 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, IS 11169 (Part 2) X12Cr13 vs BS 970 (Part 1) 410S21 is a 94.9% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 94.9%.

Frequently Compared With IS 11169 (Part 2) X12Cr13:
GOST 5632 06Kh23N28 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH GOST 5632 12Kh13 GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
94.9%
MECHANICAL MATCH
No shared data
OVERALL
94.9%
Specifications
Property IS 11169 (Part 2) X12Cr13 BS 970 (Part 1) 410S21
Standard IS 11169 (Part 2):2023 BS 970 (Part 1):1983
Category Stainless Steel Stainless Steel
C (%) 0.08-0.15 0.09-0.15
Cr (%) 11.5-13.5 11.5-13.5
Mn (%) <=1.50 <=1.0
Ni (%) <=0.75 <=1.00
P (%) <=0.040 <=0.040
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.0
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 2) X12Cr13 BS 970 (Part 1) 410S21
Reduction of Area, soft annealed (+A) >=60% (over 5 to 100 mm) Not specified
Tensile Strength, soft annealed (+A) <=600 MPa (over 5 to 100 mm) Not specified
Typical Applications
IS 11169 (Part 2) X12Cr13
Cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 100 mm (clause 1.1, Table 14)
BS 970 (Part 1) 410S21
Stainless and heat resisting steel for mechanical and allied engineering purposes (Table 13).
Can IS 11169 (Part 2) X12Cr13 Be Substituted With BS 970 (Part 1) 410S21?
IS 11169 (Part 2) X12Cr13 and BS 970 (Part 1) 410S21 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 1) 410S21 is often considered as a substitute for IS 11169 (Part 2) X12Cr13 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 11169 (Part 2) X12Cr13
0 active listings and RFQs →
BS 970 (Part 1) 410S21
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 2) X12Cr13 and BS 970 (Part 1) 410S21?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 11169 (Part 2) X12Cr13 be substituted with BS 970 (Part 1) 410S21?
IS 11169 (Part 2) X12Cr13 and BS 970 (Part 1) 410S21 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 1) 410S21 is often considered as a substitute for IS 11169 (Part 2) X12Cr13 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.