IS 11169 (Part 2) X12Cr13 vs EN 10088-1 X12Cr13

Strong Match — 98.6% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 2) X12Cr13 (IS 11169 (Part 2):2023) and EN 10088-1 X12Cr13 (EN 10088-1:2023) are both steel grades. Both fall under the Stainless Steel category. IS 11169 (Part 2) X12Cr13 is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 X12Cr13 is defined under European Standard (EN), originating from Europe.

As per chemical composition, IS 11169 (Part 2) X12Cr13 vs EN 10088-1 X12Cr13 is a 98.6% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 98.6%.

Frequently Compared With IS 11169 (Part 2) X12Cr13:
GOST 5632 06Kh23N28 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12Ni2Mo GOST 5632 12Kh13
Match Breakdown
CHEMISTRY MATCH
98.6%
MECHANICAL MATCH
No shared data
OVERALL
98.6%
Specifications
Property IS 11169 (Part 2) X12Cr13 EN 10088-1 X12Cr13
Standard IS 11169 (Part 2):2023 EN 10088-1:2023
Category Stainless Steel Stainless Steel
C (%) 0.08-0.15 0.08-0.15
Cr (%) 11.5-13.5 11.5-13.5
Mn (%) <=1.50 <=1.50
Ni (%) <=0.75 <=0.75
P (%) <=0.040 <=0.040
S (%) <=0.030 <=0.015
Si (%) <=1.00 <=1.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 2) X12Cr13 EN 10088-1 X12Cr13
Reduction of Area, soft annealed (+A) >=60% (over 5 to 100 mm) Not specified
Tensile Strength, soft annealed (+A) <=600 MPa (over 5 to 100 mm) Not specified
Typical Applications
IS 11169 (Part 2) X12Cr13
Cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 100 mm (clause 1.1, Table 14)
EN 10088-1 X12Cr13
Not documented
Can IS 11169 (Part 2) X12Cr13 Be Substituted With EN 10088-1 X12Cr13?
IS 11169 (Part 2) X12Cr13 and EN 10088-1 X12Cr13 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X12Cr13 is often considered as a substitute for IS 11169 (Part 2) X12Cr13 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 11169 (Part 2) X12Cr13
0 active listings and RFQs →
EN 10088-1 X12Cr13
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 2) X12Cr13 and EN 10088-1 X12Cr13?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 11169 (Part 2) X12Cr13 be substituted with EN 10088-1 X12Cr13?
IS 11169 (Part 2) X12Cr13 and EN 10088-1 X12Cr13 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X12Cr13 is often considered as a substitute for IS 11169 (Part 2) X12Cr13 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.