IS 1570 (Part 2/Sec 1) 10C4 vs BS 970 (Part 3) 045A10

Strong Match — 88.6% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 2/Sec 1) 10C4 (IS 1570 (Part 2/Sec 1):1979) and BS 970 (Part 3) 045A10 (BS 970 (Part 3):1991) are both steel grades. Both fall under the Carbon Steel category. IS 1570 (Part 2/Sec 1) 10C4 is typically used for wire for wood screws, welding electrode core wire and case hardened parts (the standard links this grade to is 1812, is 2879, is 4432), while BS 970 (Part 3) 045A10 is commonly used for bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; case hardening steel, carbon and carbon manganese (table 14). IS 1570 (Part 2/Sec 1) 10C4 is defined under Bureau of Indian Standards (IS), originating from India, while BS 970 (Part 3) 045A10 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, IS 1570 (Part 2/Sec 1) 10C4 vs BS 970 (Part 3) 045A10 is a 88.6% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 88.6%.

Frequently Compared With IS 1570 (Part 2/Sec 1) 10C4:
BS 970 (Part 1) 040A10 BS 970 (Part 3) 070M55 BS 970 (Part 1) 080A20 BS 970 (Part 1) 040A04 BS 970 (Part 1) 040A12 BS 970 (Part 1) 045A10 BS 970 (Part 1) 045M10 BS 970 (Part 1) 045M10 BS 970 (Part 1) 055M15 BS 970 (Part 1) 045A10 BS 970 (Part 3) 045M10 BS 970 (Part 1) 060A32
Match Breakdown
CHEMISTRY MATCH
88.6%
MECHANICAL MATCH
No shared data
OVERALL
88.6%
Specifications
Property IS 1570 (Part 2/Sec 1) 10C4 BS 970 (Part 3) 045A10
Standard IS 1570 (Part 2/Sec 1):1979 BS 970 (Part 3):1991
Category Carbon Steel Carbon Steel
C (%) <=0.15 0.08-0.13
Mn (%) 0.30-0.60 0.30-0.60
Si (%) Not specified 0.10-0.40
P (%) Not specified <=0.05
S (%) Not specified <=0.05
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 2/Sec 1) 10C4 BS 970 (Part 3) 045A10
Tensile Strength 340-420 MPa Not specified
Elongation >=26% Not specified
Typical Applications
IS 1570 (Part 2/Sec 1) 10C4
Wire for wood screws, welding electrode core wire and case hardened parts (the standard links this grade to IS 1812, IS 2879, IS 4432)
BS 970 (Part 3) 045A10
Bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; case hardening steel, carbon and carbon manganese (Table 14)
Key Differences
Can IS 1570 (Part 2/Sec 1) 10C4 Be Substituted With BS 970 (Part 3) 045A10?
IS 1570 (Part 2/Sec 1) 10C4 and BS 970 (Part 3) 045A10 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 3) 045A10 is often considered as a substitute for IS 1570 (Part 2/Sec 1) 10C4 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 1570 (Part 2/Sec 1) 10C4
0 active listings and RFQs →
BS 970 (Part 3) 045A10
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 2/Sec 1) 10C4 and BS 970 (Part 3) 045A10?
BS 970 (Part 3) 045A10 specifies Si, P, S which are not specified for IS 1570 (Part 2/Sec 1) 10C4.
Can IS 1570 (Part 2/Sec 1) 10C4 be substituted with BS 970 (Part 3) 045A10?
IS 1570 (Part 2/Sec 1) 10C4 and BS 970 (Part 3) 045A10 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 3) 045A10 is often considered as a substitute for IS 1570 (Part 2/Sec 1) 10C4 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.