IS 1570 (Part 2/Sec 1) 15C8 vs IS 11169 (Part 1) 15C8

Strong Match — 100% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 2/Sec 1) 15C8 (IS 1570 (Part 2/Sec 1):1979) and IS 11169 (Part 1) 15C8 (IS 11169 (Part 1):1984) are both steel grades. Both fall under the Carbon Steel category. IS 1570 (Part 2/Sec 1) 15C8 is typically used for boiler billets, bars and sections, welded round link chains, billets and bars for forgings, carbon steel forgings and case hardened parts (the standard links this grade to is 2100, is 6967, is 1875, is 2004, is 4432), while IS 11169 (Part 1) 15C8 is commonly used for cold heading and cold extrusion; the standard covers wires, wire rods and bars of 2 to 100 mm diameter (clause 1.1). IS 1570 (Part 2/Sec 1) 15C8 is defined under Bureau of Indian Standards (IS), originating from India, while IS 11169 (Part 1) 15C8 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 1570 (Part 2/Sec 1) 15C8 vs IS 11169 (Part 1) 15C8 is a 100% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 100%.

Frequently Compared With IS 1570 (Part 2/Sec 1) 15C8:
BS 970 (Part 1) 040A10 BS 970 (Part 3) 070M55 BS 970 (Part 1) 045M10 BS 970 (Part 1) 045A10 BS 970 (Part 1) 055M15 BS 970 (Part 1) 040A04 BS 970 (Part 3) 045A10 BS 970 (Part 1) 045M10 BS 970 (Part 3) 045M10 BS 970 (Part 1) 040A12 BS 970 (Part 1) 045A10 BS 970 (Part 1) 060A32
Match Breakdown
CHEMISTRY MATCH
100%
MECHANICAL MATCH
No shared data
OVERALL
100%
Specifications
Property IS 1570 (Part 2/Sec 1) 15C8 IS 11169 (Part 1) 15C8
Standard IS 1570 (Part 2/Sec 1):1979 IS 11169 (Part 1):1984
Category Carbon Steel Carbon Steel
C (%) 0.10-0.20 0.10-0.20
Mn (%) 0.60-0.90 0.60-0.90
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 2/Sec 1) 15C8 IS 11169 (Part 1) 15C8
Tensile Strength 420-500 MPa Not specified
Elongation >=25% Not specified
Hardness, annealed Not specified <=140 HB
Typical Applications
IS 1570 (Part 2/Sec 1) 15C8
Boiler billets, bars and sections, welded round link chains, billets and bars for forgings, carbon steel forgings and case hardened parts (the standard links this grade to IS 2100, IS 6967, IS 1875, IS 2004, IS 4432)
IS 11169 (Part 1) 15C8
Cold heading and cold extrusion; the standard covers wires, wire rods and bars of 2 to 100 mm diameter (clause 1.1)
Can IS 1570 (Part 2/Sec 1) 15C8 Be Substituted With IS 11169 (Part 1) 15C8?
IS 1570 (Part 2/Sec 1) 15C8 and IS 11169 (Part 1) 15C8 overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 1) 15C8 is often considered as a substitute for IS 1570 (Part 2/Sec 1) 15C8 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 1570 (Part 2/Sec 1) 15C8
0 active listings and RFQs →
IS 11169 (Part 1) 15C8
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 2/Sec 1) 15C8 and IS 11169 (Part 1) 15C8?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 1570 (Part 2/Sec 1) 15C8 be substituted with IS 11169 (Part 1) 15C8?
IS 1570 (Part 2/Sec 1) 15C8 and IS 11169 (Part 1) 15C8 overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 1) 15C8 is often considered as a substitute for IS 1570 (Part 2/Sec 1) 15C8 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.