IS 1570 (Part 2/Sec 1) 35C8 vs BS 970 (Part 1) 045M10

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 2/Sec 1) 35C8 (IS 1570 (Part 2/Sec 1):1979) and BS 970 (Part 1) 045M10 (BS 970 (Part 1):1983) are both steel grades. Both fall under the Carbon Steel category. IS 1570 (Part 2/Sec 1) 35C8 is typically used for billets and bars for forgings, carbon steel forgings, flame and induction hardened parts and hardened and tempered parts (the standard links this grade to is 1875, is 2004, is 3930, is 5517), while BS 970 (Part 1) 045M10 is commonly used for case hardening steel for mechanical and allied engineering purposes (table 11 mechanical properties).. IS 1570 (Part 2/Sec 1) 35C8 is defined under Bureau of Indian Standards (IS), originating from India, while BS 970 (Part 1) 045M10 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, IS 1570 (Part 2/Sec 1) 35C8 vs BS 970 (Part 1) 045M10 is a 85.7% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With IS 1570 (Part 2/Sec 1) 35C8:
BS 970 (Part 3) 070M55 BS 970 (Part 1) 040A10 BS 970 (Part 1) 080A20 BS 970 (Part 1) 045M10 BS 970 (Part 1) 040A12 BS 970 (Part 3) 045A10 BS 970 (Part 1) 040A04 BS 970 (Part 1) 045A10 BS 970 (Part 1) 045A10 BS 970 (Part 3) 045M10 BS 970 (Part 1) 055M15 BS 970 (Part 1) 060A32
Match Breakdown
CHEMISTRY MATCH
85.7%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property IS 1570 (Part 2/Sec 1) 35C8 BS 970 (Part 1) 045M10
Standard IS 1570 (Part 2/Sec 1):1979 BS 970 (Part 1):1983
Category Carbon Steel Carbon Steel
C (%) 0.30-0.40 0.07-0.13
Mn (%) 0.60-0.90 0.30-0.60
P (%) Not specified <=0.050
S (%) Not specified <=0.050
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 2/Sec 1) 35C8 BS 970 (Part 1) 045M10
Tensile Strength 550-650 MPa Not specified
Elongation >=20% Not specified
Typical Applications
IS 1570 (Part 2/Sec 1) 35C8
Billets and bars for forgings, carbon steel forgings, flame and induction hardened parts and hardened and tempered parts (the standard links this grade to IS 1875, IS 2004, IS 3930, IS 5517)
BS 970 (Part 1) 045M10
Case hardening steel for mechanical and allied engineering purposes (Table 11 mechanical properties).
Key Differences
Can IS 1570 (Part 2/Sec 1) 35C8 Be Substituted With BS 970 (Part 1) 045M10?
IS 1570 (Part 2/Sec 1) 35C8 and BS 970 (Part 1) 045M10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
IS 1570 (Part 2/Sec 1) 35C8
0 active listings and RFQs →
BS 970 (Part 1) 045M10
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 2/Sec 1) 35C8 and BS 970 (Part 1) 045M10?
BS 970 (Part 1) 045M10 specifies P, S which are not specified for IS 1570 (Part 2/Sec 1) 35C8.
Can IS 1570 (Part 2/Sec 1) 35C8 be substituted with BS 970 (Part 1) 045M10?
IS 1570 (Part 2/Sec 1) 35C8 and BS 970 (Part 1) 045M10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.