IS 1570 (Part 2/Sec 1) 35C8 vs BS 970 (Part 1) 080A20

Close Alternative — 84.9% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 2/Sec 1) 35C8 (IS 1570 (Part 2/Sec 1):1979) and BS 970 (Part 1) 080A20 (BS 970 (Part 1):1991) are both steel grades. Both fall under the Carbon Steel category. IS 1570 (Part 2/Sec 1) 35C8 is typically used for billets and bars for forgings, carbon steel forgings, flame and induction hardened parts and hardened and tempered parts (the standard links this grade to is 1875, is 2004, is 3930, is 5517), while BS 970 (Part 1) 080A20 is commonly used for used for nuts, bolts, hydraulic fittings, precision turned parts, sleeves, and couplings.. IS 1570 (Part 2/Sec 1) 35C8 is defined under Bureau of Indian Standards (IS), originating from India, while BS 970 (Part 1) 080A20 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, IS 1570 (Part 2/Sec 1) 35C8 vs BS 970 (Part 1) 080A20 is a 89.5% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 84.9%.

Frequently Compared With IS 1570 (Part 2/Sec 1) 35C8:
BS 970 (Part 3) 070M55 BS 970 (Part 1) 040A10 BS 970 (Part 1) 045M10 BS 970 (Part 1) 040A12 BS 970 (Part 3) 045A10 BS 970 (Part 1) 040A04 BS 970 (Part 1) 045A10 BS 970 (Part 1) 045M10 BS 970 (Part 3) 045M10 BS 970 (Part 1) 055M15 BS 970 (Part 1) 060A32 BS 970 (Part 1) 045A10
Match Breakdown
CHEMISTRY MATCH
89.5%
MECHANICAL MATCH
No shared data
OVERALL
84.9%
Specifications
Property IS 1570 (Part 2/Sec 1) 35C8 BS 970 (Part 1) 080A20
Standard IS 1570 (Part 2/Sec 1):1979 BS 970 (Part 1):1991
Category Carbon Steel Carbon Steel
C (%) 0.30-0.40 0.18-0.23
Mn (%) 0.60-0.90 0.70-0.90
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 2/Sec 1) 35C8 BS 970 (Part 1) 080A20
Tensile Strength 550-650 MPa Not specified
Elongation >=20% Not specified
Typical Applications
IS 1570 (Part 2/Sec 1) 35C8
Billets and bars for forgings, carbon steel forgings, flame and induction hardened parts and hardened and tempered parts (the standard links this grade to IS 1875, IS 2004, IS 3930, IS 5517)
BS 970 (Part 1) 080A20
Used for nuts, bolts, hydraulic fittings, precision turned parts, sleeves, and couplings.
Can IS 1570 (Part 2/Sec 1) 35C8 Be Substituted With BS 970 (Part 1) 080A20?
IS 1570 (Part 2/Sec 1) 35C8 and BS 970 (Part 1) 080A20 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
Forms & Sizes Available on M-EX
IS 1570 (Part 2/Sec 1) 35C8
No active listings currently.
BS 970 (Part 1) 080A20
Round Bar → (2 listings)
Diameter: 40–40 mm (1.57–1.57 in)
Length: 4800–6600 mm (188.98–259.84 in)
On M-EX Right Now
IS 1570 (Part 2/Sec 1) 35C8
0 active listings and RFQs →
BS 970 (Part 1) 080A20
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 2/Sec 1) 35C8 and BS 970 (Part 1) 080A20?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 1570 (Part 2/Sec 1) 35C8 be substituted with BS 970 (Part 1) 080A20?
IS 1570 (Part 2/Sec 1) 35C8 and BS 970 (Part 1) 080A20 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.