IS 1570 (Part 3) 11C10S25 vs IS 1570 (Part 3) 10C8S10

Close Alternative — 70.4% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 3) 11C10S25 (IS 1570 (Part 3):1979) and IS 1570 (Part 3) 10C8S10 (IS 1570 (Part 3):1979) are both steel grades. Both fall under the Free Machining Steel category. IS 1570 (Part 3) 11C10S25 is defined under Bureau of Indian Standards (IS), originating from India, while IS 1570 (Part 3) 10C8S10 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 1570 (Part 3) 11C10S25 vs IS 1570 (Part 3) 10C8S10 is a 80.7% match. As per mechanical properties, the match is 50%. Combined, this makes them a close alternative overall at 70.4%.

Frequently Compared With IS 1570 (Part 3) 11C10S25:
SAE J403 1117 IS 4432 10C8S10 SAE J403 1117 SAE J403 1118 SAE J403 1126 SAE J403 1117 SAE J403 1118 SAE J403 1126 SAE J403 1118 SAE J403 1126 SAE J403 1132 SAE J403 1132
Match Breakdown
CHEMISTRY MATCH
80.7%
MECHANICAL MATCH
50%
OVERALL
70.4%
Specifications
Property IS 1570 (Part 3) 11C10S25 IS 1570 (Part 3) 10C8S10
Standard IS 1570 (Part 3):1979 IS 1570 (Part 3):1979
Category Free Machining Steel Free Machining Steel
C (%) 0.08-0.15 <=0.15
Si (%) <=0.10 0.05-0.30
Mn (%) 0.80-1.20 0.60-0.90
P (%) <=0.060 <=0.060
S (%) 0.20-0.30 0.08-0.13
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 3) 11C10S25 IS 1570 (Part 3) 10C8S10
Tensile Strength 370-490 MPa 370-490 MPa
Elongation >=22% >=24%
Condition Hot rolled or normalized bars, billets and forgings (Table 2), ruling sections up to 150 mm Hot rolled or normalized bars, billets and forgings (Table 2), ruling sections up to 150 mm
Can IS 1570 (Part 3) 11C10S25 Be Substituted With IS 1570 (Part 3) 10C8S10?
IS 1570 (Part 3) 11C10S25 and IS 1570 (Part 3) 10C8S10 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
IS 1570 (Part 3) 11C10S25
0 active listings and RFQs →
IS 1570 (Part 3) 10C8S10
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 3) 11C10S25 and IS 1570 (Part 3) 10C8S10?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 1570 (Part 3) 11C10S25 be substituted with IS 1570 (Part 3) 10C8S10?
IS 1570 (Part 3) 11C10S25 and IS 1570 (Part 3) 10C8S10 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.