IS 1570 (Part 3) 11C10S25 vs SAE J403 1118

Close Alternative — 76.2% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 3) 11C10S25 (IS 1570 (Part 3):1979) and SAE J403 1118 (SAE J403:2009) are both steel grades. Both fall under the Free Machining Steel category. IS 1570 (Part 3) 11C10S25 is defined under Bureau of Indian Standards (IS), originating from India, while SAE J403 1118 is defined under SAE International, originating from United States.

As per chemical composition, IS 1570 (Part 3) 11C10S25 vs SAE J403 1118 is a 76.2% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 76.2%.

Frequently Compared With IS 1570 (Part 3) 11C10S25:
IS 1570 (Part 3) 10C8S10 SAE J403 1117 IS 4432 10C8S10 SAE J403 1117 SAE J403 1118 SAE J403 1126 SAE J403 1117 SAE J403 1126 SAE J403 1118 SAE J403 1126 SAE J403 1132 SAE J403 1132
Match Breakdown
CHEMISTRY MATCH
76.2%
MECHANICAL MATCH
No shared data
OVERALL
76.2%
Specifications
Property IS 1570 (Part 3) 11C10S25 SAE J403 1118
Standard IS 1570 (Part 3):1979 SAE J403:2009
Category Free Machining Steel Free Machining Steel
C (%) 0.08-0.15 0.14-0.20
Si (%) <=0.10 Not specified
Mn (%) 0.80-1.20 1.30-1.60
P (%) <=0.060 <=0.030
S (%) 0.20-0.30 0.08-0.13
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 3) 11C10S25 SAE J403 1118
Tensile Strength 370-490 MPa Not specified
Elongation >=22% Not specified
Condition Hot rolled or normalized bars, billets and forgings (Table 2), ruling sections up to 150 mm Not specified
Typical Applications
IS 1570 (Part 3) 11C10S25
Not documented
SAE J403 1118
Chemistry-only grade; product scope as listed in the composition notes
Key Differences
Can IS 1570 (Part 3) 11C10S25 Be Substituted With SAE J403 1118?
IS 1570 (Part 3) 11C10S25 and SAE J403 1118 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
IS 1570 (Part 3) 11C10S25
0 active listings and RFQs →
SAE J403 1118
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 3) 11C10S25 and SAE J403 1118?
IS 1570 (Part 3) 11C10S25 specifies Si which is not specified for SAE J403 1118.
Can IS 1570 (Part 3) 11C10S25 be substituted with SAE J403 1118?
IS 1570 (Part 3) 11C10S25 and SAE J403 1118 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.