IS 1570 (Part 4) 103Cr6 vs GOST 801 ShKh15

Strong Match — 90.5% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 4) 103Cr6 (IS 1570 (Part 4):1988) and GOST 801 ShKh15 (GOST 801-1978) are both steel grades. Both fall under the Alloy Steel category. IS 1570 (Part 4) 103Cr6 is defined under Bureau of Indian Standards (IS) (India).

As per chemical composition, IS 1570 (Part 4) 103Cr6 vs GOST 801 ShKh15 is a 90.5% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 90.5%.

Frequently Compared With IS 1570 (Part 4) 103Cr6:
IS 1570 (Part 4) 10Mo6 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 7) 10Cr36Mo10H GOST 4543 12HN3A NF A35-565 100C6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 7) 12Cr2Mo5V2H UNI 11234 100Cr6 IS 1570 (Part 7) 10Mo6H IS 11169 (Part 1) 10Ni5Cr4
Match Breakdown
CHEMISTRY MATCH
90.5%
MECHANICAL MATCH
No shared data
OVERALL
90.5%
Specifications
Property IS 1570 (Part 4) 103Cr6 GOST 801 ShKh15
Standard IS 1570 (Part 4):1988 GOST 801-1978
Category Alloy Steel Alloy Steel
C (%) 0.95-1.10 0.95-1.05
Si (%) 0.10-0.35 0.17-0.37
Mn (%) 0.25-0.45 0.2-0.5
Cr (%) 1.40-1.60 1.35-1.65
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 4) 103Cr6 GOST 801 ShKh15
Tensile Strength Not specified 750-950 MPa
Yield Strength Not specified 450 MPa min
Elongation Not specified 8% min
Hardness Not specified 60-66 HRC
Typical Applications
IS 1570 (Part 4) 103Cr6
Not documented
GOST 801 ShKh15
Used for ball bearings, roller bearings, races, bearing rings, and precision rollers.
Can IS 1570 (Part 4) 103Cr6 Be Substituted With GOST 801 ShKh15?
IS 1570 (Part 4) 103Cr6 and GOST 801 ShKh15 overlap closely enough on chemistry and mechanical properties that GOST 801 ShKh15 is often considered as a substitute for IS 1570 (Part 4) 103Cr6 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
Forms & Sizes Available on M-EX
IS 1570 (Part 4) 103Cr6
No active listings currently.
GOST 801 ShKh15
Round Bar → (2 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 6600–7000 mm (259.84–275.59 in)
On M-EX Right Now
IS 1570 (Part 4) 103Cr6
0 active listings and RFQs →
GOST 801 ShKh15
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 4) 103Cr6 and GOST 801 ShKh15?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 1570 (Part 4) 103Cr6 be substituted with GOST 801 ShKh15?
IS 1570 (Part 4) 103Cr6 and GOST 801 ShKh15 overlap closely enough on chemistry and mechanical properties that GOST 801 ShKh15 is often considered as a substitute for IS 1570 (Part 4) 103Cr6 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.