IS 1570 (Part 4) 15Cr6Ni6 vs EN 10084 17CrNi6-6

Strong Match — 86% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 4) 15Cr6Ni6 (IS 1570 (Part 4):1988) and EN 10084 17CrNi6-6 (EN 10084:2008) are both steel grades. Both fall under the Alloy Steel category. IS 1570 (Part 4) 15Cr6Ni6 is defined under Bureau of Indian Standards (IS), originating from India, while EN 10084 17CrNi6-6 is defined under European Standard (EN), originating from Europe.

As per chemical composition, IS 1570 (Part 4) 15Cr6Ni6 vs EN 10084 17CrNi6-6 is a 86% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 86%.

Frequently Compared With IS 1570 (Part 4) 15Cr6Ni6:
GB/T 3077 12Cr2Ni4A IS 1570 (Part 4) 10Cr20Mo6 GOST 4543 12HN3A IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 105Cr5 IS 11169 (Part 1) 12Ni3Cr2 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 103Cr6 IS 11169 (Part 1) 10Ni5Cr4 NF A35-565 100C6 UNI 11234 100Cr6 IS 1570 (Part 4) 10Mo6
Match Breakdown
CHEMISTRY MATCH
86%
MECHANICAL MATCH
No shared data
OVERALL
86%
Specifications
Property IS 1570 (Part 4) 15Cr6Ni6 EN 10084 17CrNi6-6
Standard IS 1570 (Part 4):1988 EN 10084:2008
Category Alloy Steel Alloy Steel
C (%) 0.12-0.18 0.14-0.20
Si (%) 0.15-0.35 <=0.40
Mn (%) 0.40-0.60 0.50-0.90
Ni (%) 1.40-1.70 1.40-1.70
Cr (%) 1.40-1.70 1.40-1.70
P (%) Not specified <=0.025
S (%) Not specified <=0.035
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 4) 15Cr6Ni6 EN 10084 17CrNi6-6
Condition Not specified Soft annealed
Hardenability Not specified +H band at 1.5 mm from the quenched end: 39 to 47 HRC
Hardness Not specified Soft annealed: 229 HB max
Typical Applications
IS 1570 (Part 4) 15Cr6Ni6
Not documented
EN 10084 17CrNi6-6
Case hardened machine parts: carburized or carbonitrided, then hardened (clause 3.1)
Key Differences
Can IS 1570 (Part 4) 15Cr6Ni6 Be Substituted With EN 10084 17CrNi6-6?
IS 1570 (Part 4) 15Cr6Ni6 and EN 10084 17CrNi6-6 overlap closely enough on chemistry and mechanical properties that EN 10084 17CrNi6-6 is often considered as a substitute for IS 1570 (Part 4) 15Cr6Ni6 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 1570 (Part 4) 15Cr6Ni6
0 active listings and RFQs →
EN 10084 17CrNi6-6
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 4) 15Cr6Ni6 and EN 10084 17CrNi6-6?
EN 10084 17CrNi6-6 specifies P, S which are not specified for IS 1570 (Part 4) 15Cr6Ni6.
Can IS 1570 (Part 4) 15Cr6Ni6 be substituted with EN 10084 17CrNi6-6?
IS 1570 (Part 4) 15Cr6Ni6 and EN 10084 17CrNi6-6 overlap closely enough on chemistry and mechanical properties that EN 10084 17CrNi6-6 is often considered as a substitute for IS 1570 (Part 4) 15Cr6Ni6 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.