Related Material — 69.9% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 4) 35Cr5Mo6V2 (IS 1570 (Part 4):1988) and IS 1570 (Part 4) 15Cr13Mo6 (IS 1570 (Part 4):1988) are both steel grades. Both fall under the Alloy Steel category. IS 1570 (Part 4) 35Cr5Mo6V2 is defined under Bureau of Indian Standards (IS), originating from India, while IS 1570 (Part 4) 15Cr13Mo6 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 1570 (Part 4) 35Cr5Mo6V2 vs IS 1570 (Part 4) 15Cr13Mo6 is a 71.1% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With IS 1570 (Part 4) 35Cr5Mo6V2:
NF A35-565 100C6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 07Cr4Mo6 UNI 11234 100Cr6 IS 1570 (Part 4) 105Cr5 IS 4367 10Cr9Mo10 IS 4367 07Cr4Mo6 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 10Mo6 IS 1570 (Part 4) 10Cr20Mo6 GB/T 3077 12Cr2Ni4A GOST 4543 12HN3A
Match Breakdown
CHEMISTRY MATCH
71.1%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property IS 1570 (Part 4) 35Cr5Mo6V2 IS 1570 (Part 4) 15Cr13Mo6
Standard IS 1570 (Part 4):1988 IS 1570 (Part 4):1988
Category Alloy Steel Alloy Steel
C (%) 0.25-0.45 0.10-0.20
Si (%) 0.10-0.35 0.15-0.35
Mn (%) 0.40-0.70 0.40-0.70
Ni (%) <=0.30 <=0.30
Cr (%) 1.00-1.50 2.90-3.40
Mo (%) 0.50-0.80 0.45-0.65
V (%) 0.20-0.30 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 4) 35Cr5Mo6V2 IS 1570 (Part 4) 15Cr13Mo6
Tensile Strength Not specified >=1540 MPa
Yield Strength Not specified >=1240 MPa (0.2 % proof stress)
Elongation Not specified >=8%
Izod Impact Not specified >=14 J
Hardness Not specified >=444 HBS (guidance only)
Condition Not specified Bars and forgings, hardened and tempered (oil hardened unless stated), limiting ruling section 63 mm
Key Differences
Can IS 1570 (Part 4) 35Cr5Mo6V2 Be Substituted With IS 1570 (Part 4) 15Cr13Mo6?
IS 1570 (Part 4) 35Cr5Mo6V2 and IS 1570 (Part 4) 15Cr13Mo6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
IS 1570 (Part 4) 35Cr5Mo6V2
0 active listings and RFQs →
IS 1570 (Part 4) 15Cr13Mo6
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 4) 35Cr5Mo6V2 and IS 1570 (Part 4) 15Cr13Mo6?
IS 1570 (Part 4) 35Cr5Mo6V2 specifies V which is not specified for IS 1570 (Part 4) 15Cr13Mo6.
Can IS 1570 (Part 4) 35Cr5Mo6V2 be substituted with IS 1570 (Part 4) 15Cr13Mo6?
IS 1570 (Part 4) 35Cr5Mo6V2 and IS 1570 (Part 4) 15Cr13Mo6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.