IS 1570 (Part 4) 55Cr3 vs NF A35-565 100C6

Related Material — 58.8% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 4) 55Cr3 (IS 1570 (Part 4):1988) and NF A35-565 100C6 are both steel grades. Both fall under the Alloy Steel category. IS 1570 (Part 4) 55Cr3 is defined under Bureau of Indian Standards (IS), originating from India, while NF A35-565 100C6 is defined under Association Francaise de Normalisation (NF), originating from France.

As per chemical composition, IS 1570 (Part 4) 55Cr3 vs NF A35-565 100C6 is a 73.3% match. As per mechanical properties, the match is 30%. Combined, this makes them a related material overall at 58.8%.

Frequently Compared With IS 1570 (Part 4) 55Cr3:
IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 10Mo6 IS 4367 07Cr4Mo6 IS 1570 (Part 4) 07Cr4Mo6 UNI 11234 100Cr6 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 7) 10Cr36Mo10H IS 4367 10Cr9Mo10 EN 10028-2 10CrMo9-10 IS 1570 (Part 7) 10Mo6H
Match Breakdown
CHEMISTRY MATCH
73.3%
MECHANICAL MATCH
30%
OVERALL
58.8%
Specifications
Property IS 1570 (Part 4) 55Cr3 NF A35-565 100C6
Standard IS 1570 (Part 4):1988 NF A35-565
Category Alloy Steel Alloy Steel
C (%) 0.50-0.60 0.95-1.05
Si (%) 0.10-0.35 0.15-0.35
Mn (%) 0.60-0.80 0.25-0.45
Cr (%) 0.60-0.80 1.35-1.65
S (%) Not specified <=0.025
P (%) Not specified <=0.027
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 4) 55Cr3 NF A35-565 100C6
Tensile Strength 890-1040 MPa 850-1100 MPa
Yield Strength >=650 MPa (0.2 % proof stress) Not specified
Elongation >=12% Not specified
Izod Impact >=35 J Not specified
Hardness 255-311 HBS (guidance only) 60-66 HRC
Condition Wear resisting steel, hardened and tempered, limiting ruling section 63 mm Not specified
Typical Applications
IS 1570 (Part 4) 55Cr3
Not documented
NF A35-565 100C6
ball bearings, roller bearings, bearing races, rollers, precision tools, wear resistant parts
Key Differences
Can IS 1570 (Part 4) 55Cr3 Be Substituted With NF A35-565 100C6?
IS 1570 (Part 4) 55Cr3 and NF A35-565 100C6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 1570 (Part 4) 55Cr3
No active listings currently.
NF A35-565 100C6
Round Bar → (2 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 6700–6700 mm (263.78–263.78 in)
On M-EX Right Now
IS 1570 (Part 4) 55Cr3
0 active listings and RFQs →
NF A35-565 100C6
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 4) 55Cr3 and NF A35-565 100C6?
NF A35-565 100C6 specifies S, P which are not specified for IS 1570 (Part 4) 55Cr3.
Can IS 1570 (Part 4) 55Cr3 be substituted with NF A35-565 100C6?
IS 1570 (Part 4) 55Cr3 and NF A35-565 100C6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.