IS 1570 (Part 5) X02Cr17Ni12Mo2 vs ASTM A959 26-3-3

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 5) X02Cr17Ni12Mo2 (IS 1570 (Part 5):1985) and ASTM A959 26-3-3 (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 5) X02Cr17Ni12Mo2 is defined under Bureau of Indian Standards (IS), originating from India, while ASTM A959 26-3-3 is defined under ASTM International, originating from United States.

As per chemical composition, IS 1570 (Part 5) X02Cr17Ni12Mo2 vs ASTM A959 26-3-3 is a 70.8% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With IS 1570 (Part 5) X02Cr17Ni12Mo2:
ASTM A959 29-4C EN 10088-1 1.4401 GOST 5632 06Kh23N28 GOST 5632 12Kh13 EN 10088-1 1.4006 GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 EN 10088-1 1.4301 EN 10088-1 1.4845 ASTM A959 .- IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH
Match Breakdown
CHEMISTRY MATCH
70.8%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property IS 1570 (Part 5) X02Cr17Ni12Mo2 ASTM A959 26-3-3
Standard IS 1570 (Part 5):1985 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Si (%) <=1.0 <=1.00
Mn (%) <=2.0 <=1.00
P (%) <=0.045 <=0.040
S (%) <=0.030 <=0.030
Cr (%) 16.0-18.0 25.0-28.0
Ni (%) 10.0-14.0 1.0-3.5
Mo (%) 2.0-3.0 3.0-4.0
N (%) Not specified <=0.040
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 5) X02Cr17Ni12Mo2 ASTM A959 26-3-3
Tensile Strength >=485 MPa Not specified
Yield Strength >=170 MPa (0.2 % proof stress) Not specified
Elongation >=40% (50 mm) Not specified
Hardness <=217 HB; <=95 HRB Not specified
Condition Annealed, quenched or solution treated plates, sheets and strips (Table 2) Not specified
Typical Applications
IS 1570 (Part 5) X02Cr17Ni12Mo2
Not documented
ASTM A959 26-3-3
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can IS 1570 (Part 5) X02Cr17Ni12Mo2 Be Substituted With ASTM A959 26-3-3?
IS 1570 (Part 5) X02Cr17Ni12Mo2 and ASTM A959 26-3-3 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
IS 1570 (Part 5) X02Cr17Ni12Mo2
0 active listings and RFQs →
ASTM A959 26-3-3
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 5) X02Cr17Ni12Mo2 and ASTM A959 26-3-3?
ASTM A959 26-3-3 specifies N which is not specified for IS 1570 (Part 5) X02Cr17Ni12Mo2.
Can IS 1570 (Part 5) X02Cr17Ni12Mo2 be substituted with ASTM A959 26-3-3?
IS 1570 (Part 5) X02Cr17Ni12Mo2 and ASTM A959 26-3-3 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.