IS 1570 (Part 5) X02Cr17Ni12Mo2 vs GB/T 3280 06Cr19Ni10

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 5) X02Cr17Ni12Mo2 (IS 1570 (Part 5):1985) and GB/T 3280 06Cr19Ni10 (GB/T 3280-2015) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 5) X02Cr17Ni12Mo2 is defined under Bureau of Indian Standards (IS), originating from India, while GB/T 3280 06Cr19Ni10 is defined under Guobiao Standards (GB/T), originating from China.

As per chemical composition, IS 1570 (Part 5) X02Cr17Ni12Mo2 vs GB/T 3280 06Cr19Ni10 is a 71.2% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With IS 1570 (Part 5) X02Cr17Ni12Mo2:
ASTM A959 29-4C ASTM A959 26-3-3 EN 10088-1 1.4401 GOST 5632 06Kh23N28 GOST 5632 12Kh13 EN 10088-1 1.4006 GOST 5632 08X18H10 EN 10088-1 1.4301 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH ASTM A959 .-
Match Breakdown
CHEMISTRY MATCH
71.2%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property IS 1570 (Part 5) X02Cr17Ni12Mo2 GB/T 3280 06Cr19Ni10
Standard IS 1570 (Part 5):1985 GB/T 3280-2015
Category Stainless Steel Stainless Steel
C (%) <=0.030 0.08 max
Si (%) <=1.0 1.00 max
Mn (%) <=2.0 2.00 max
P (%) <=0.045 0.045 max
S (%) <=0.030 0.030 max
Cr (%) 16.0-18.0 18.00-20.00
Ni (%) 10.0-14.0 8.00-11.00
Mo (%) 2.0-3.0 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 5) X02Cr17Ni12Mo2 GB/T 3280 06Cr19Ni10
Tensile Strength >=485 MPa 520-720 MPa
Yield Strength >=170 MPa (0.2 % proof stress) 205-310 MPa
Elongation >=40% (50 mm) 40-60%
Hardness <=217 HB; <=95 HRB 187 HB max
Condition Annealed, quenched or solution treated plates, sheets and strips (Table 2) Not specified
Typical Applications
IS 1570 (Part 5) X02Cr17Ni12Mo2
Not documented
GB/T 3280 06Cr19Ni10
Used for kitchen equipment, food processing machinery, chemical tanks, piping, architectural panels, and fasteners.
Key Differences
Can IS 1570 (Part 5) X02Cr17Ni12Mo2 Be Substituted With GB/T 3280 06Cr19Ni10?
IS 1570 (Part 5) X02Cr17Ni12Mo2 and GB/T 3280 06Cr19Ni10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 1570 (Part 5) X02Cr17Ni12Mo2
No active listings currently.
GB/T 3280 06Cr19Ni10
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2900–3300 mm (114.17–129.92 in)
On M-EX Right Now
IS 1570 (Part 5) X02Cr17Ni12Mo2
0 active listings and RFQs →
GB/T 3280 06Cr19Ni10
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 5) X02Cr17Ni12Mo2 and GB/T 3280 06Cr19Ni10?
IS 1570 (Part 5) X02Cr17Ni12Mo2 specifies Mo which is not specified for GB/T 3280 06Cr19Ni10.
Can IS 1570 (Part 5) X02Cr17Ni12Mo2 be substituted with GB/T 3280 06Cr19Ni10?
IS 1570 (Part 5) X02Cr17Ni12Mo2 and GB/T 3280 06Cr19Ni10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.